Quick Links - Click To Jump To Section:

• Features & Benefits
• Preparation
• Application

Features & Benefits

• High-build, flexible, water-borne, acrylic dispersion based paint
• Contains zinc phosphate as anticorrosive pigment
• Dries to a tough and corrosion protecting coating
• Especially suited for application by airless spray
• Direct-to-metal coat in water-borne paint systems, ie. under bridges
• Service temperature: - Maximum, dry exposure only: 120°C

Preparation

• Cleanliness:
  • Remove oil, grease and other contaminants by suitable detergent cleaning
  • Remove salts, detergents and other contaminants by high pressure fresh water cleaning
• New build:
  • Abrasive blasting to min. Sa 2½ (ISO 8501-1) / SP 10 (SSPC)
  • Remove dust, blast media and loose materials

Application

• Stir well before use
• Thinner: Fresh water. Cleaner: Fresh water
• Apply with brush, roller or airless spray (Nozzle pressure: 180 bar [2600 psi] Nozzle orifice: 0.015-0.019")
• Dry film thickness: 60-120 micron (80 recommended)
• Wet film thickness: 150-275 micron (190 recommended)
• Coverage: 3.5m²/L - 7.1m²/L (5.3m²/L recommended)
• Touch dry in 18 minutes @ 20°C
• Surface dry in 50 minutes @ 20°C
• Hard dry in 100 minutes @ 20°C
• Through dry in 14 hours @ 20°C
• Fully cured in 7 days @ 20°C

If brush or roller application is used, more coats will be necessary to achieve the specified dry film thickness. Spray data are indicative and subject to adjustment. Pressure is for a material temperature of 20°C.

Product may be specified in another film thickness than indicated depending on purpose and area of use. This will alter spreading rate, drying and curing time and overcoating interval. For best performance, avoid excessive film thickness.

To obtain the drying time stated, it is important to maintain sufficient ventilation during application, drying and curing. Condensation on the freshly applied coating should be avoided. The surface must be dry and clean prior to application.