Tikkurila Fontecryl AP is a water-borne, one-component fast-drying acrylic based primer for various surfaces containing active anti-corrosive pigments.
- Provides excellent adhesion
- Used as an anti-corrosive primer on steel, aluminium and zinc surfaces
- Suitable for dipping
- Can be overcoated both with water and solvent-borne topcoats
- Wide range of colours available
- Drying times can be shortened by using higher temperatures
- Recommended to be used in processing industry and agriculture and earth moving equipment
Tikkurila Fontecryl AP is a water-borne, one-component fast-drying acrylic based primer for various surfaces containing active anticorrosive pigments.
Fontecryl AP provides excellent adhesion and is used as an anti-corrosive primer on steel, aluminium and zinc surfaces.
Due to its good wetting and levelling properties, Fontecryl AP is also suitable for dipping applications.
Fontecryl AP can be overcoated both with water and solvent-borne topcoats.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoat
- Application Conditions
- Application
- Thinner/Cleaning
- VOC
- Health And Safety
Features & Benefits
- Provides excellent adhesion and is used as an anti-corrosive primer on steel, aluminium and zinc surfaces
- Due to its good wetting and levelling properties, Fontecryl AP is also suitable for dipping applications
- Can be overcoated both with water and solvent-borne topcoats
- The product provides protection comparable to that of solvent borne epoxy paint
- Wide range of colours available
- Drying times can be shortened by using higher temperatures
- Recommended to be used in processing industry and agriculture and earth moving equipment
Technical Data
- Volume Solids: 33±2% (ISO 3233)
- Weight Solids: 45±2%
- Specific Gravity: 1.2 kg / l
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
125µm | 40µm | 8.3 m²/l |
Recommended film thicknesses | Theoretical coverage | |
Wet | Dry | |
60µm | 20µm | 16.5 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 40µm | 15°C | 23°C | 35°C |
---|---|---|---|
Dust dry, after | 2h | 30min | 5min |
Touch dry, after | 2½h | 1h | 15min |
Recoatable, min. after | 24h | 1–2 h | 30min |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation
Surface Preparation
Oil, grease, salt and dirt are removed from the surface by appropriate means.
Steel Surfaces
- Blast clean to grade Sa2½. (ISO 8501-1)
- If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Zinc Surfaces
- Sweep blast clean with mineral abrasives, e.g. quartz sand, to an even roughness. (SaS, SFS 5873).
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
- For hot dip galvanized surfaces see separate application instructions.
Aluminium Surfaces
- Sweep blast clean with non-metallic abrasives to an even roughness. (SaS, SFS 5873).
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Panssaripesu detergent.
- If sweep blasting is not possible, the surface should be roughened by hand abrading or washed with Maalipesu detergent.
Recommended Primers
Fontecryl AP.
Recommended Topcoat
Application Conditions
- All surfaces must be clean, dry and free from contamination.
- The temperature of the ambient air, surface and paint should not fall below +15ºC during application and drying.
- Relative humidity of the air should be between 20–70%.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Application
Spraying
- The product is thinned approximately 0–15%.
- Recommended nozzle tip is 0.011"–0.015" and pressure 120–160 bar.
- Spray angle shall be chosen according to the shape of the object.
Dip Coating
- The product is thinned 7–15% to the viscosity 20–25s (DIN4).
Brush Application
- The product should be thinned according to the circumstances.
Mix the product properly in case of sedimentation or viscosity increase.
Note! The viscosity falls quickly when thinning the paint.
Thinner/Cleaning
Thinner
Water.
Cleaning Of Equipment
Clean the spraying equipment immediately after use as follows:
- Run the equipment with water to remove excess paint from the equipment.
- Run the equipment with a mixture of approx 20% Thinner 1053 in clean water, at least two times.
- Finally wash with undiluted Thinner 1053.
Wash the equipment with water before starting to paint again. Unwashed equipment can cause serious surface defects.
VOC
The Volatile Organic Compounds amount is 120 g/litre of paint. VOC content in paint (thinned 15% by volume) is 100 g/l.
Health And Safety
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial and professional use only.
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Data sheet
- Manufacturer
- Tikkurila
- Water / Solvent Based
- Water
- For Use On
- Steel, aluminium, zinc
- Application Method
- Brush, spray, Dip Coating
- Sheen
- Matt
- Colour
- Standard / Ready Mixed
- VOC Levels
- Low (50-149 g/l)
- Single, Two or Three Pack
- Single
- Pack Size
- 20L
- Base Type
- Acrylic Based
- Solvent
- Mixture (se Safety Data Sheet)
- Coverage
- 8.3 m²/l
- Recommended Thinner/Cleaner
- Water
- Min. Application Temperature
- 15ºC
- Solids by Volume
- 33±2% (ISO 3233)
- VOC
- 100 g/l
- Recommended Dry Film Thickness
- 40µm
- Recommended Wet Film Thickness
- 125µm
- UN Number
- UN3082
- Dry to Recoat (at 23°C)
- 1-2hrs
- Touch Dry (at 23°C)
- 1hr
- Base Type
- Water-Based
- Base Type
- Acrylic
- Suitable For Use On
- Zinc
- Suitable For Use On
- Aluminium
- Suitable For Use On
- Steel
- Suitable For Use On
- Galvanised Steel
- Finish
- Matt
- Application Method
- Brush
- Application Method
- Spray
- Application Method
- Dip
- Usages
- Atmospheric
- Usages
- Anti-Corrosive
- Product Usage Type
- Primer
- Product Range
- Fontecryl
- Colour Family
- Grey
- Colour Family
- Red
- Colour Family
- Black
- Dry to Recoat (@ 20-25°C)
- 2 hours
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Fontecryl AP is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Duasolid 50
Tikkurila Duasolid 50, a two-component, high-solids oxirane ester paint containing active anti-corrosive pigments. This eco-friendly alternative to epoxy and polyurethane paints is suitable for earth moving machines, haulage and lifting equipment, forklifts, agricultural machinery, electric appliances, pumps and other steel structures,...
Tikkurila Fontedur HB 80
Tikkurila Fontedur HB 80, a two-component, water-borne polyurethane topcoat for use on steel surfaces exposed to weathering, abrasion and chemical stress. Recommended to be used for agricultural and earth moving machinery, steel framework and other steel structures, machinery and equipment. Huge colour range available from RAL, BS & NCS...
Tikkurila Fontelac QD 80
Tikkurila Fontelac QD 80 is a water-borne, one-component glossy topcoat based on alkyd dispersion ideal for touch-up painting in indoor areas. Used as a glossy finish for small tanks, agricultural machinery, haulage equipment and other machinery and equipment. Easy to use - one-component Ideal for touch-up painting in indoor areas Wide...
Tikkurila Temadur SC-F 20
Tikkurila Temadur SC-F 20, recommended especially to be used as a single coat finish for agricultural and earth moving machinery and other machinery and equipment, with active anti-corrosive pigments that ensure corrosion resistance even in severe climatic conditions. Can help speed up the painting process and decrease the overall costs of...
Tikkurila Temadur SC-F 50
Tikkurila Temadur SC-F 50, a 2-component fast-drying semi-gloss polyurethane paint with excellent weathering and abrasion resistance, recommended especially to be used as a single coat finish for agricultural and earth moving machinery and other machinery and equipment. Huge range of colours available from RAL, BS & NCS Also suitable...
Tikkurila Temadur SC-F 80
Tikkurila Temadur SC-F 80, a two-component fast-drying glossy polyurethane paint, containing anti-corrosive pigments, developed for single-coat painting agricultural and earth-moving machinery. Huge range of colours available from RAL, BS & NCS Meets the requirements set in Volvo STD 423-0014, accelerated corrosion test for 6 weeks...
Tikkurila Thinner 1053
Tikkurila Thinner 1053 is a slow thinner for alkyd paints, chlorinated rubber paints and 1-component acrylic paints. For use with recommended Tikkurila products.
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...