PPG SigmaCover 380 is a universal epoxy anticorrosive primer, based upon pure epoxy technology.
- Universal pure epoxy primer system suitable for ballast tanks, decks, topside, superstructures and hulls
- Good abrasion resistance for dedicated areas of application
- Suitable for immersion service (ballast tanks, outside shell)
- Good anticorrosive properties and water resistance
- Good flexibility
- Resistant to well designed cathodic protection
- Good drying and curing property
- Suitable for both newbuilding and maintenance applications
Description
PPG SigmaCover 380 is a universal epoxy anticorrosive primer, based upon pure epoxy technology.
Click To Jump To Section:
- Features & Benefits
- Product Specification
- Film Thickness Range
- Drying Times
- Surface Preparation
- Application Methods
- Product Notes
- Health & Safety
Features & Benefits
- Universal pure epoxy primer system suitable for ballast tanks, decks, topside, superstructure and hull
- Good abrasion resistance for dedicated areas of application
- Suitable for immersion service (ballast tanks, outside shell)
- Good anticorrosive properties and water resistance
- Good flexibility
- Resistant to well designed cathodic protection
- Good drying and curing property
- Suitable for both newbuilding and maintenance applications
Product Specification
| Technical Data | ||||||
|---|---|---|---|---|---|---|
| PPG SigmaCover 380 | ||||||
| Number of Components: | Two | |||||
| Mass Density: | 1.4 kg/l (11.7 lb/US gal) | |||||
| Volume Solids: | 83 ± 2% | |||||
| VOC (supplied): | Directive 1999/13/EC, SED: max. 161.0 g/kg) max. 226.0 g/l (approx. 1.9 lb/US gal) | |||||
| Recommended Dry Film Thickness: | 125 - 200 μm (5.0 - 8.0 mils) depending on system | |||||
| Theoretical Spreading Rate: | 6.4 m²/l for 125 μm (257 ft²/US gal for 5.0 mils) | |||||
| Shelf Life: | Base: at least 24 months when stored cool and dry | |||||
| Hardener: at least 24 months when stored cool and dry | ||||||
Film Thickness Range
| Spreading Rate & Film Thickness | |||
|---|---|---|---|
| DFT | Theoretical Spreading Rate | ||
| 125 μm (5.0 mils) | 6.4 m²/l (257 ft²/US gal) | ||
| 160 μm (6.3 mils) | 5.0 m²/l (204 ft²/US gal) | ||
| 200 μm (8.0 mils) | 4.0 m²/l (160 ft²/US gal) | ||
Note:
- Maximum DFT in critical areas, applied in two equal coats: 1500 μm (60.0 mils).
Drying Times
| Drying Times At 20°C | |||
|---|---|---|---|
| Substrate temperature | Dry To Touch | Dry To Handle | Fully Cured |
| 5°C (41°F) | 24 hours | 48 hours | 20 days |
| 10°C (50°F) | 12 hours | 24 hours | 14 days |
| 20°C (68°F) | 3 hours | 8 hours | 7 days |
| 30°C (86°F) | 2 hours | 6 hours | 4 days |
| 40°C (104°F) | 1 hour | 4 hours | 3 days |
Notes:
- Adequate ventilation must be maintained during application and curing.
| Overcoating interval for DFT up to 150μm (6.0mils) | ||||||
|---|---|---|---|---|---|---|
| Overcoating with: | Interval: | 5°C (41°F) | 10°C (50°F) | 20°C (68°F) | 30°C (86°F) | 40°C (104°F) |
| Itself | ||||||
| Minimum | 48 hours | 24 hours | 8 hours | 4 hours | 2 hours | |
| Maximum | 28 days | 28 days | 28 days | 28 days | 28 days | |
Notes:
- Surface should be dry and free from any contamination.
Surface Preparation
Immersion Exposure
- Steel or steel with not appoved zinc silicate shop primer: blast cleaned to ISO-Sa2½, blasting profile 30 - 75 μm (1.2 – 3.0 mils).
- Steel with approved zinc silicate shop primer; weld seams and areas of damaged shop primer or breakdown should be blast cleaned to ISO-Sa2½, blasting profile 30 - 75 μm (1.2 – 3.0 mils) or power tool cleaned to SPSS-Pt3.
- Coated steel; hydrojetted to VIS WJ2L (blasting profile 30 – 75 μm (1.2 – 3.0 mils).
- Previous coat must be dry and free from any contamination.
IMO-MSC.215(82) Requirements For Water Ballast Tanks
- Steel; ISO 8501-3: 2006 grade P2, with all edges treated to a rounded radius of minimum 2 mm (0.0789 in) or subject to three pass grinding.
- Steel or steel with not appoved zinc silicate shop primer: blast cleaned to ISO-Sa2½, blasting profile 30 - 75 μm (1.2 – 3.0 mils).
- Steel with approved zinc silicate shop primer; weld seams and areas of shop primer damage or break down should be blast cleaned to Iso-Sa 2½ blasting profile 30 – 75 μm (1.2 – 3.0 mils): [1] For shop primer with IMO type approval; no additional requirements; [2] For shop primer without IMO type approval; blast cleaned to ISO-Sa2 removing at least 70% of intact shop primer, blasting profile 30 – 75 μm (1.2 – 3.0 mils).
- Damages up to 2% of the total area of the tank may be treated to ISO-St3. Damages over 2% of the total area of the tank or contiguous damages over 25 m² (269 ft²) have to be blast cleaned to ISO-Sa2½.
- Dust quantity rating "1 for dust size class "3", "4" or "5", lower dust size classes to be removed if visible on the surface to be coated without magnification (ISO 8502-3:1992).
- Previous coat must be dry and free from any contamination.
Atmospheric Exposure Conditions
- Steel; pretreated preferably to ISO-Sa2½, , blasting profile 30 – 75 μm (1.2 – 3.0 mils) or according to ISO-St3.
- Shop primed steel; pretreated to SPSS-Pt3.
- Galvanized steel must be free from grease, salts and any contamination.
- Galvanized steel must be sweep blasted or otherwise roughened.
- Coated steel; hydrojetted to VIS WJ2L (blasting profile 30 – 75 μm (1.2 – 3.0 mils).
- Previous coat must be dry and free from any contamination.
Substrate Temperature & Application Conditions
- Substrate temperature during application and curing should be above 5°C (41°F).
- Substrate temperature during application and curing should be at least 3°C (5°F) above dew point.
- Relative humidity during application and curing should not exceed 85%.
Application Methods
Mixing Ratio By Volume: Base To Hardener 80:20 (4:1)
- The temperature of the mixed base and hardener should preferably be above 15°C (59°F), otherwise extra thinner may be required to obtain application viscosity.
- Adding too much thinner results in reduced sag resistance and slower cure.
- Thinner should be added after mixing the components.
Induction Time:
- None
Pot Life:
- 4 hours at 20°C (68°F)
Airless Spray:
- Recommended Thinner: THINNER 91-92
- Volume Of Thinner: 0 - 10%, depending on required thickness and application conditions
- Nozzle Orifice: Approx. 0.46 – 0.53 mm (0.018 – 0.021 in)
- Nozzle Pressure: 20.0 - 25.0 MPa (approx. 200 - 250 bar; 2901 - 3626 p.s.i.)
Brush/Roller:
- Brush: for stripe coating and spot repair only
Cleaning Solvent
Product Notes
| Information On Basic Physical And Chemical Properties | ||||||
|---|---|---|---|---|---|---|
| PPG SigmaCover 380 Base | PPG SigmaCover 380 Hardener | |||||
| Form: | Liquid | Liquid | ||||
| Colour: | Various | Clear | ||||
| Odour: | Aromatic | Aromatic | ||||
| Odour Threshold: | Not available | Not available | ||||
| pH-value 20°C: | Insoluble in water. | Insoluble in water. | ||||
| Melting point/freezing point: | May start to solidify at the following temperature: <-7°C (<19.4°F) This is based on data for the following ingredient: 4-nonylphenol, branched. Weighted average:-61.03°C (-77.9°F) | May start to solidify at the following temperature: -15.4°C (4.3°F) This is based on data for the following ingredient: benzyl alcohol. Weighted average: -71.08°C (-95.9°F) | ||||
| Initial boiling point and boiling range: | >37.78°C | >37.78°C | ||||
| Flash Point: | Closed cup: 38°C | Closed cup: 29°C | ||||
| Evaporation Rate: | Highest known value: 0.84 (ethylbenzene) Weighted average: 0.74compared with butyl acetate | Highest known value: 0.84 (ethylbenzene) Weighted average: 0.58compared with butyl acetate | ||||
| Flammability (solid, gas): | liquid | liquid | ||||
| Upper/lower flammability or : explosive limits: | Greatest known range: Lower: 1.7% Upper: 10.9% (2-methylpropan-1-ol) | Greatest known range: Lower: 1.3% Upper: 13% (benzyl alcohol) | ||||
| Vapour pressure: | Highest known value: <1.6 kPa (<12 mm Hg) (at 20°C) (2-methylpropan-1-ol). Weighted average: 0.83 kPa (6.23 mm Hg) (at 20°C) | Highest known value: <1.6 kPa (<12 mm Hg) (at 20°C) (2-methylpropan-1-ol). Weighted average: 0.63 kPa (4.73 mm Hg) (at 20°C) | ||||
| Vapour Density: | Highest known value: 7.59 (Air = 1) (4-nonylphenol, branched). Weighted average: 4.59 (Air = 1) | Highest known value: 3.7 (Air = 1) (ethylbenzene). Weighted average: 3.34 (Air = 1) | ||||
| Relative density: | 1.54 | 0.93 | ||||
| Solubility(ies): | Insoluble in the following materials: cold water | Insoluble in the following materials: cold water | ||||
| Partition coefficient: n-octanol/ water: | Not applicable | Not applicable | ||||
| Auto-ignition temperature: | Lowest known value: 372°C (701.6°F) (4-nonylphenol, branched) | Lowest known value: 382°C (719.6°F) (2,4,6-tris(dimethylaminomethyl)phenol | ||||
| Decomposition temperature: | Stable under recommended storage and handling conditions | Stable under recommended storage and handling conditions | ||||
| Viscosity: | Kinematic (40°C): >0.21 cm² /s - 60 - 100 s (ISO 6mm) | Kinematic (40°C): >0.21 cm² /s | ||||
| Explosive properties: | The product itself is not explosive, but the formation of an explosible mixture of vapour or dust with air is possible. | The product itself is not explosive, but the formation of an explosible mixture of vapour or dust with air is possible. | ||||
| Oxidising properties: | Product does not present an oxidizing hazard | Product does not present an oxidizing hazard | ||||
Health & Safety
- This is a solvent-borne paint and care should be taken to avoid inhalation of spray mist or vapor, as well as contact between the wet paint and exposed skin or eyes.
- For further information please see the safety data sheets in the attachments section above.
Product Details
4784-1037658
Data sheet
- Manufacturer
- PPG
- For Use On
- Steel
- Application Method
- Brush, Roller, Spray
- Sheen
- Eggshell
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 4L, 20L
- Mixing Ratio
- Base To Hardener 80:20 (4:1)
- Application
- Brush, Roller, Spray
- Touch Dry (at 20°C)
- 3 hours
- Dry to Handle (at 20°C)
- 8 hours
- Fully Cured (at 20°C)
- 7 days
- Coverage
- 6.4 m²/l for 125 μm (257 ft²/US gal for 5.0 mils)
- Recommended Thinner/Cleaner
- THINNER 91-92 - Cleaner: THINNER 90-53
- Min. Application Temperature
- 5°C (41°F)
- Density
- 1.4 kg/l (11.7 lb/US gal)
- Solids by Volume
- 83 ± 2%
- VOC
- Directive 1999/13/EC, SED: max. 161.0 g/kg) max. 226.0 g/l (approx. 1.9 lb/US gal)
- Shelf Life (from date of manufacture)
- Base: at least 24 months when stored cool and dry. Hardener: at least 24 months when stored cool and dry.
- Finish
- Eggshell
- Size
- 4L & 5L
- Recommended Dry Film Thickness
- 125 - 200 μm (5.0 - 8.0 mils) depending on system
- UN Number
- UN1263
- UN Number
- Hardener: UN3469
- Dry to Handle (at 10°C)
- 24 hours
- Fully Cured (at 10°C)
- 14 days
- Touch Dry (at 10°C)
- 12 hours
- Pot Life
- 4 hours at 20°C (68°F)
- Suitable For Use On
- Steel
- Finish
- Eggshell
- Application Method
- Brush
- Application Method
- Roller
- Application Method
- Spray
- Product Usage Type
- Primer
- Product Range
- SigmaCover
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Black
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
PPG SigmaCover 380 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT