Tikkurila Temasilox | High-solids and high-gloss anti corrosive topcoat for steel substrates

Tikkurila Temasilox

Reference 99V

Brand Tikkurila

Search ID TIK4794

Tikkurila Temasilox is a high performance, isocyanate free two-component, high-solids and high-gloss polysiloxane topcoat. Ideal for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.

Huge colour range available.
Excellent anti-corrosive properties.
When applied in two-coat system on zinc rich primer, corrosivity class C5 can be achieved.
As a high-solids, VOC compliant product Temasilox meets even the most stringent environmental demands.
Higher UV-resistance than with conventional topcoats.
Can also be used as a single-coat finish on blast cleaned or phosphated steel. On blast cleaned steel even corrosivity category C4 is possible.

Product customisation

Don't forget to save your customization to be able to add to cart

Colour Group

Size

Finish

£920.33(incl. VAT)

£766.94(ex. VAT)

Quantity

Please choose your colour

Available for Delivery (See Delivery Options Below)

ColourPicker Explained

In general we sort colours for products into 2 main groups - ‘Ready Mixed’ and ‘Tinted’.
Tinted colours will always be more expensive than Ready Mixed colours as they need to be produced at the time of order using a tinting machine dispensing colourant into a base*.
During busy periods, this means that tinted colours could take longer, for example – a ready mixed colour ordered on a 3-5 day delivery might arrive within 3 days, however a tinted colour might take the full 5 days to arrive.

To find Ready Mixed colours, search "ready mixed" or select the Ready Mixed 'colour chart'. To see Tinted colours select a colour chart such as RAL, BS, NCS, etc. or search for a colour/hue to see available or related options.

To ensure fair pricing, we split colours into ‘Price Bands’ to group together similar priced colours. If you wish to search for the cheapest tinted colours, always select Price Band 1.

We make every effort to list all available colours, however we also offer a colour match service which can be accessed by contacting our Technical Team on 0113 245 5450 (option 2) or emailing [email protected]

*Colours are sold in the nearest tin size but actual paint volume per tin may vary up to 10% depending on colour

Colour reproduction of the Products on the Site is limited by the technology used to deliver web pages and by the colour representation of Customer’s own monitor and computer set-up. We have made every effort to display as accurately as possible the colours of our Products but we cannot guarantee that the colour shown on Customer’s monitor’s display will accurately reflect the colour of the Product on delivery. We recommend that Customer first purchases the smallest Product available or access an industry standard colour chart in person (and not digitally) to ensure that the colour is acceptable for its purposes.

No queries yet, leave the first!

Description

Tikkurila Temasilox is a high performance, two-component, high-solids and high-gloss polysiloxane topcoat with excellent colour and gloss retention.

Recommended to be used as an isocyanate free finishing coating for steel structures for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.

The anti-corrosive properties of Temasilox are outstanding. The product can be used as a single-coat paint or a topcoat. When applied in a two-coat system on zinc-rich primer, corrosivity class C5 can be achieved.

Temasilox is isocyanate free and does not, therefore, generate any di-isocyanates during cutting, welding or in a fire. The product promotes a healthier working environment and has less impact on the environment.

As a high-solids, VOC-compliant product, Temasilox meets even the most stringent environmental demands. Using Temasilox instead of conventional topcoats will result in a remarkable reduction in solvent emissions.

Features & Benefits

Huge colour range available.
Excellent anticorrosive properties. When applied in two-coat system on zinc rich primer, corrosivity class C5 can be achieved.
Isocyanate free topcoat. Does not generate any di-isocyanates during cutting, welding or in a fire.
As a high-solids, VOC compliant product Temasilox meets even the most stringent environmental demands.
Higher UV-resistance than with conventional topcoats.
Offers significant savings with regard to maintenance costs.
Easy to apply on large surfaces due to long open time of the paint film.
No need for evaporation of solvents before ovening.
Rapidly ready for service.
The product is approved to be used as a topcoat in pre-qualified systems according to NORSOK M-501, system 1, rev.6.
Can also be used as a single-coat finish on blast cleaned or phosphated steel. On blast cleaned steel even corrosivity category C4 is possible.
Recommended to be used as an isocyanate free finishing coating for steel structures for bridges, tanks, pipes, buildings, power plants, offshore structures and other structures that require long durability in severe corrosive atmospheric areas.

Technical Data

Volume Solids: 87±2%.

Weight Solids:91±2%.

Specific Gravity: 1.5±0.1 kg / l (mixed).

Mixing Ratio:

Base - 2 parts by volume - Temasilox.
Hardener - 1 part by volume - 008 7601.

Pot Life (23°C): 2 hours.

Recommended Film Thicknesses and Theoretical Coverage:

Recommended film thicknesses		Theoretical coverage
Wet	Dry
90µm	80µm	10.9 m²/l
140µm	120µm	7.3 m²/l
170µm	150µm	5.8 m²/l

Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.

Drying Time:

DFT 120 µm	5°C	10°C	23°C	50°C	70°C
Dust dry, after	1.5hrs	1hr	30min	-	-
Touch dry, after	2h	1hr 30min	1hr	-	-
Dry to handle, after	8hrs	5.5hrs	3hrs	1hr	25min

Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation. When forced drying in temperatures 50–100ºC, use flash-off time between 0–15 minutes, depending on the wet film thickness and the actual temperature.

Gloss: High Gloss.

Colour Shades: RAL, NCS, BS, White.

Surface Preparation

Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4).

Steel Surfaces:

Blast clean to grade Sa2½–3. (ISO 8501-1)
If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.

Primed Surfaces:

Oil, grease, salt and dirt are removed from the surface by appropriate means.
Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4).

Recommended Primers

Recommended Topcoats

Temasilox.

Application Conditions

All surfaces must be clean, dry and free from contamination.
The temperature of the ambient air, surface and paint should not fall below +5ºC during application and drying.
Relative humidity of the air should not exceed 80% during application and drying.
The surface temperature of steel should remain at least 3°C above the dew point.
Good ventilation and sufficient air movement is required in confined areas during application and drying.

Mixing Components

First stir base and hardener separately.
The correct proportions of base and hardener must be mixed thoroughly before use.
Use power mixer for mixing.
Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.

Application

Airless Spraying:

The product is thinned approximately 0–5% depending on the temperature of the components and shape of the object.
Recommended nozzle tip is 0.011"–0.015" and pressure 160–200 bar.
Spray angle shall be chosen according to the shape of the object.
Do not use worn-out nozzle.

Air-assisted Airless Spraying:

The product is thinned approximately 0–5% depending on the temperature of the components and shape of the object.
Recommended nozzle tip is 0.011"–0.015" and pressure 160–200 bar.
Atomising air pressure should be 1–3 bar.
Spray angle shall be chosen according to the shape of the object.
Do not use worn-out nozzle.

In order to reach DFT 120 µm it is recommended to use “wet-on-wet” technique:

First layer 100–125 µm WFT and then let the solvents evaporate for 5–15 minutes and apply the full coat. Misty first layer may result in orange peel.

For brush application the product should be thinned according to the circumstances.

Thinners

Thinner 1048, Thinner 1061.

Cleaning Of Equipment

Thinner 1048 or Thinner 1061.

VOC

The Volatile Organic Compounds amount (ISO 11890) is 130 g/litre of paint mixture. VOC content of the paint mixture (thinned 5% by volume) is 170 g/l.

Health And Safety

Further information about hazardous influences and protection are detailed in individual health and safety data sheets.

For industrial and professional use only.

Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.

Click to go back to the top of the page

Product Details

Reference 4794-773896

Data sheet

Manufacturer: Tikkurila
Interior / Exterior Use: Interior & Exterior
Single, Two or Three Pack: Two-Pack
Parts: Two
Interior/Exterior Use: Both
Solvent: Mixture (see Safety Data Sheet)
Mixing Ratio: 2:1
Suitable Substrates: Steel
Key Features: High Gloss, High Build, Excellent anticorrosive properties
Application: Spray, brush
Touch Dry (at 20°C): 60 mins
Coverage: 5.8 m²/l - 10.9 m²/l
Recommended Thinner/Cleaner: Thinner 1048, Thinner 1061
Compatible Primers: Temacoat GPL-S Primer, Temacoat Primer, Temasil 90, Temazinc 77, Temazinc 99, Temacoat HS-F Primer.
Compatible Topcoats: Temasilox
Min. Application Temperature: 5ºC
Solids by Volume: 87±2%
VOC: 170 g/l
Finish: High Gloss
Recommended Dry Film Thickness: 80µm - 150µm
Recommended Wet Film Thickness: 90µm - 170µm
UN Number (Activator): UN1263
UN Number (Base): UN1263
Touch Dry (at 23°C): 1h
Dry to Handle (at 23°C): 3h
Pot Life: 2 hours at 23°C
Specific Gravity: 1.5±0.1 kg / l (mixed)
Solids by Weight: 91±2%
Base Type: Solvent-Based
Suitable For Use On: Steel
Suitable For Use On: Primed Surfaces
Finish: High Gloss
Application Method: Brush
Application Method: Spray
Usages: Severe Exposures
Usages: Direct to Metal
Usages: High Solids
Usages: UV Resistant
Usages: Atmospheric
Usages: Anti-Corrosive
Usages: Gloss Retention
Usages: Isocyanate Free/Non-Isocyanate
Usages: Colour Retention
Usages: 1 Coat
Product Usage Type: Topcoat
Product Range: Temasilox
Colour Family: White
Colour Family: Anthracite Grey
Colour Family: Beige
Colour Family: Grey
Colour Family: Green
Colour Family: Blue
Colour Family: Red
Colour Family: Brown
Colour Family: Pink
Colour Family: Orange
Colour Family: Purple
Colour Family: Yellow
Colour Family: Black
Non - Isocyanate: Isocyanate Free/Non-Isocyanate
Product Type: Polysiloxane
Environment: Atmospheric
Environment: Severe Exposures
Touch Dry/Dust Free (@ 20-25°C): 60 mins
Product Attributes: 1 coat
Product Attributes: High Solids
Product Attributes: Anti-Corrosive
Product Attributes: Gloss Retention
Product Attributes: Colour Retention
Product Attributes: Isocyanate Free
Resistance to: UV

Attachments

Download

Product Data Sheet

Download

Safety Data Sheet (Base)

Download

Safety Data Sheet (Hardener)

Download

Temasilox Painting Instruction

Download

Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.

Questions

Question about the product

Name ^*

Email ^*

Question ^*

^* Required fields

I have read and agree to the conditions of use (read)

Be the first to ask a question about this product!

IMPORTANT SHIPPING & DELIVERY INFORMATION

Tikkurila Temasilox is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.

Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.

Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.

All delivery costs below are excluding VAT

Surface Preparation Kits for Steel

These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...

£25.93 (incl. VAT)

Shop now

In Stock and Available for Delivery

Tikkurila Temasilox