PPG Sigmadur 550 H (formerly known as Sigmadur 568) is a two-component, high solids, high-build aliphatic acrylic polyurethane finish with excellent resistance to atmospheric exposure conditions with good colour and gloss retention, resisting splash of mineral and vegetable oils, paraffins, aliphatic petroleum products and mild chemicals.
- Available in 2,300+ colours, inc. RAL, BS, NCS & the new NCS 2050 colours
- Cures at temperatures down to -5°C (23°F)
- Can be recoated even after long atmospheric exposure
- Good application properties by airless, brush and roller
- High film build-up to 150 µm (6.0 mils) for one coat
- Can be applied direct to metal
- Drying and curing times can be reduced significantly using PPG 866M ACCELERATOR
Product customisation
Don't forget to save your customization to be able to add to cartDescription
PPG Sigmadur 550 H (formerly known as Sigmadur 568), two-component, high solids, high-build aliphatic acrylic polyurethane finish available in 2,300+ colours from RAL, NCS and BS.
The finish has excellent resistance to atmospheric exposure conditions with good colour and gloss retention, resisting splash of mineral and vegetable oils, paraffins, aliphatic petroleum products and mild chemicals.
Applies directly to metal and can be recoated even after long atmospheric exposure, curing at temperatures down to -5°C (23°F).
Features & Benefits
- Available in 2,300+ colours, inc. RAL, BS, NCS & the new NCS 2050 colours
- Excellent resistance to atmospheric exposure conditions
- Good colour and gloss retention
- Cures at temperatures down to -5°C (23°F)
- Resistant to splash of mineral and vegetable oils, paraffins, aliphatic petroleum products and mild chemicals
- Can be recoated even after long atmospheric exposure
- Good application properties by airless, brush and roller
- High film build-up to 150 µm (6.0 mils) for one coat
- Can be applied direct to metal
- Drying and curing times can be reduced significantly using PPG 866M ACCELERATOR
Product Data
Two-component, high solids, high-build aliphatic acrylic polyurethane finish
| Data for mixed product at 20°C (68°F) | |
|---|---|
| Number of components | Two |
| Mass density | 1.5 kg/l (12.5 lb/US gal) |
| Volume solids | 70 ± 2% |
| VOC (Supplied) | Directive 1999/13/EC, SED: max. 220.0 g/kg |
| max. 330.0 g/l (approx. 2.8 lb/US gal) | |
| UK PG 6/23(92) Appendix 3: max. 259.0 g/l (approx. 2.2 lb/US gal) | |
| Recommended dry film thickness | 50 - 150 µm (2.0 - 6.0 mils) depending on system |
| Theoretical spreading rate | 14.0 m²/l for 50 µm (561 ft²/US gal for 2.0 mils) |
| 9.3 m²/l for 75 µm (374 ft²/US gal for 3.0 mils) | |
| Overcoating Interval | Minimum: 8 hours |
| Maximum: Unlimited | |
| Shelf life | Base: at least 36 months when stored cool and dry |
| Hardener: at least 24 months when stored cool and dry | |
Notes:
- See below for more information on surface preparation, application details and curing times
Surface Preparation
Recommended Substrate Conditions and Temperatures
Substrate conditions
- Steel; blast cleaned to ISO-Sa2½, blasting profile 40 – 70 µm (1.6 – 1.8 mils), or power tool cleaned to ISO-St3
- Compatible previous coat must be dry and free from any contamination
Substrate Temperature & Application Conditions
- Substrate temperature during application and curing should be at least 3°C (5°F) above dew point
- Substrate temperature during application and curing down to -5°C (23°F) is acceptable; provided the substrate is free from ice and dry
- Relative humidity during application and curing should not exceed 85%
- Premature exposure to early condensation and rain may cause colour and gloss change
Application
Instructions for Use
Mixing ratio by volume: base to hardener 87:13
- Do not thin more than is required by appropriate application property
- Adding too much thinner results in reduced sag resistance
- Thinner should be added after mixing the components
Induction Time
None.
Pot life
- 2.5 hours at 20°C (68°F)
Refer below for more information
Air spray
Recommended thinner
Volume of thinner
- 10 - 15%, depending on required thickness and application conditions
Nozzle orifice
- 1.0 - 1.5 mm (approx. 0.040 - 0.060 in)
Nozzle pressure
- 0.3 - 0.4 MPa (approx. 3 - 4 bar; 44 - 58 p.s.i.)
Airless spray
Recommended thinner
- THINNER 21-06
Volume of thinner
- 0 - 10%, depending on required thickness and application conditions
Nozzle orifice
- Approx. 0.43 – 0.48 mm (0.017 – 0.019 in)
Nozzle pressure
- 20.0 MPa (approx. 200 bar; 2901 p.s.i.)
Brush/roller
Recommended thinner
- THINNER 21-06
Volume of thinner
- 0 – 5%
Spreading Rate and Film Thickness
| DFT | Theoretical spreading rate |
|---|---|
| 50 µm (2.0 mils) | 14.0 m²/l (561 ft²/US gal) |
| 60 µm (2.4 mils) | 9.3 m²/l (374 ft²/US gal) |
| 100 µm (4.0 mils) | 7.0 m²/l (281 ft²/US gal) |
| 150 µm (6.0 mils) | 4.7 m²/l (187 ft²/US gal) |
Overcoating interval for DFT up to 150 µm (6.0 mils)
| Overcoating with... | Interval | -5°C (23°F) | 0°C (32°F) | 10°C (50°F) | 20°C (68°F) | 30°C (86°F) | 40°C (104°F) |
|---|---|---|---|---|---|---|---|
| Itself | Minimum | 36 hours | 24 hours | 16 hours | 8 hours | 4 hours | 3 hours |
| Maximum | Unlimited | Unlimited | Unlimited | Unlimited | Unlimited | Unlimited |
Overcoating interval with PPG 866M ACCELERATOR for DFT up to 150 µm (6.0 mils)
| Overcoating with... | Interval | -5°C (23°F) | 0°C (32°F) | 10°C (50°F) | 20°C (68°F) | 30°C (86°F) | 40°C (104°F) |
|---|---|---|---|---|---|---|---|
| Itself | Minimum | 28 hours | 20 hours | 12 hours | 6 hours | 3 hours | 1.5 hours |
| Maximum | Unlimited | Unlimited | Unlimited | Unlimited | Unlimited | Unlimited |
Note: Surface should be dry and free from any contamination
Curing time for DFT up to 150 μm (6.0 mils)
| Substrate temperature | Dry to touch | Dry to handle | Full cure |
|---|---|---|---|
| -5°C (23°F) | 24 hours | 40 hours | 22 days |
| 0°C (32°F) | 15 hours | 30 hours | 18 days |
| 10°C (50°F) | 5 hours | 20 hours | 10 days |
| 20°C (68°F) | 3 hours | 12 hours | 7 days |
| 30°C (86°F) | 2 hours | 6 hours | 4 days |
| 40°C (104°F) | 1 hour | 3 hours | 3 days |
Curing time with PPG 866M ACCELERATOR for DFT up to 150 µm (6.0 mils)
| Substrate temperature | Dry to touch | Dry to handle | Full cure |
|---|---|---|---|
| -5°C (23°F) | 21 hours | 32 hours | 18 days |
| 0°C (32°F) | 12 hours | 24 hours | 15 days |
| 10°C (50°F) | 4 hours | 15 hours | 8 days |
| 20°C (68°F) | 2 hours | 8 hours | 6 days |
| 30°C (86°F) | 1.5 hours | 4 hours | 3 days |
| 40°C (104°F) | 1 hour | 2 hours | 48 hours |
Notes:
- Adequate ventilation must be maintained during application and curing (please refer to INFORMATION SHEETS)
- Safe Working in Confined Spaces (1433) and Directives for Ventilation Practice (1434)
- Premature exposure to early condensation and rain may cause colour and gloss change
Pot Life (at application viscosity)
| Mixed product temperature | Pot life |
|---|---|
| 10°C (50°F) | 4 hours |
| 20°C (68°F) | 2.5 hours |
| 30°C (86°F) | 1.5 hours |
| 40°C (104°F) | 1 hour |
Note:
- Mixing this product with PPG 866M ACCELERATOR will not affect the pot life
Safety Precautions
- For paint and recommended thinners, see information sheets information sheet 1430, information sheet 1431 and the relevant Material Safety Data Sheets in the attachments section above
- This is a solvent-borne paint and care should be taken to avoid inhalation of spray mist or vapour, as well as contact between the wet paint and exposed skin or eyes
- Contains a toxic polyisocyanate curing agent
- Avoid at all times inhalation of aerosol spray mist
References
- Explanation to product data sheets (information sheet 1411)
- Safety Indicators (information sheet 1430)
- Safety in Confined Space and Health Safety, Explosion Hazard - Toxic Hazard (information sheet 1431)
- Safe Working in Confined Spaces (information sheet 1433)
- Directives for Ventilation Practice (information sheet 1434)
Product Details
4155-893220
Data sheet
- Manufacturer
- PPG
- Water / Solvent Based
- Solvent
- For Use On
- Metal
- Application Method
- Brush, Roller, Spray
- Sheen
- Gloss
- Colour
- Fully Tintable
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 4L, 20L
- Parts
- 2
- Solvent
- Aliphatic acrylic polyurethane
- Mixing Ratio
- 87:13
- Suitable Substrates
- Metal
- Key Features
- Direct to metal, low curing, 350+ colours, chemical splash resistant
- Application
- Brush, Roller, Spray
- Touch Dry (at 20°C)
- 3 hours
- Dry to Handle (at 20°C)
- -
- Dry to Recoat (at 20°C)
- 8 hours
- Fully Cured (at 20°C)
- 7 days
- Pot Life (at 20°C)
- 2.5 hours
- Coverage
- 14.0 m²/l for 50 µm (561 ft²/US gal for 2.0 mils) 9.3 m²/l for 75 µm (374 ft²/US gal for 3.0 mils)
- Recommended Thinner/Cleaner
- THINNER 21-06
- Unit Contents
- Base & hardener
- Compatible Primers
- -
- Compatible Topcoats
- -
- Max. Application Temperature
- -
- Min. Application Temperature
- -5°C (23°F)
- Density
- 1.5 kg/l (12.5 lb/US gal)
- Solids by Volume
- 70 ± 2%
- Heat Resistance (up-to)
- -
- VOC
- Directive 1999/13/EC, SED: max. 220.0 g/kg max. 330.0 g/l - UK PG 6/23(92) Appendix 3: max. 259.0 g/l
- Shelf Life (from date of manufacture)
- Base: at least 36 months - Hardener: at least 24 months.
- UN Number (Activator)
- -
- UN Number (Base)
- UN1263
- Base Type
- Solvent-Based
- Suitable For Use On
- Metal
- Suitable For Use On
- Steel
- Suitable For Use On
- Compatible Existing Coatings
- Finish
- Gloss
- Application Method
- Brush
- Application Method
- Roller
- Application Method
- Spray
- Usages
- Low Temperature
- Usages
- Atmospheric
- Usages
- Gloss Retention
- Usages
- Colour Retention
- Usages
- Overcoatable
- Usages
- Direct to Metal
- Usages
- High Solids
- Usages
- Chemical Resistance
- Usages
- High Build
- Product Usage Type
- Topcoat
- Product Range
- SigmaDur
- Colour Family
- Purple
- Colour Family
- Yellow
- Colour Family
- Black
- Colour Family
- White
- Colour Family
- Neutral
- Colour Family
- Anthracite Grey
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Colour Family
- Pink
- Colour Family
- Orange
- Categorised As
- Metal Paints > Low Temperature Direct-to-Metal Paints
- Seasonal
- Cold Weather
- Product Type
- Acrylic Polyurethane
- Environment
- Atmospheric
- Environment
- Low Temperature
- Touch Dry/Dust Free (@ 20-25°C)
- 3 hours
- Product Attributes
- High Build
- Product Attributes
- High Solids
- Product Attributes
- Gloss Retention
- Product Attributes
- Colour Retention
- Product Attributes
- Overcoatable
- Resistance to
- Chemicals
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
PPG SigmaDur 550 H is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
You might also like