International Intergard 263

FAJ034
INT4810

International Intergard 263, a two pack, tar free, epoxy tie coat for use between anticorrosives and either antifoulings or cosmetic finishes, ensuring maximum system adhesion and performance on outside shell vessel areas.

  • Use as a sealer coat over Tributyltin (TBT) antifoulings
  • For use at newbuilding, maintenance & repair or on board maintenance
  • Can be overcoated with a large range of compatible products
  • Certified; forms a barrier to for TBT leaching from an underlying TBT antifouling when used as part of an approved system
Colour
Size
Finish
£404.83(incl. VAT)
£337.36(ex. VAT)
Quantity
Please choose your colour
Available for Delivery (See Delivery Options Below)

Description

International Intergard 263 is a two pack, tar free, epoxy tie coat for use between anticorrosives and either antifoulings or cosmetic finishes to ensure maximum system adhesion and performance on outside shell vessel areas.

Can also be used as a sealer coat over Tributyltin (TBT) antifoulings.

For use at newbuilding, maintenance & repair or on board maintenance.



Quick Links - Click To Jump To Section:




Features & Benefits


  • 2 pack
  • Tar-free
  • Used as a tie coat between anticorrosives and either antifoulings or cosmetic finishes
  • Ensures maximum system adhesion and performance on outside shell vessel areas
  • Use as a sealer coat over Tributyltin (TBT) antifoulings
  • For use at newbuilding, maintenance & repair or on board maintenance
  • Certified; forms a barrier to for TBT leaching from an underlying TBT antifouling when used as part of an approved system



Product Information


Colour

  • FAJ034-Light Grey

(See Systems and Compatibility section)

 

Finish/Sheen

  • Matt

 

Part B (Curing Agent)

  • FAA262

 

Volume Solids

  • 57% ±2% (ISO 3233:1998)

 

Mix Ratio

  • 4 volume(s) Part A to 1 volume(s) Part B

 

Typical Film Thickness

  • 100 microns dry (175 microns wet)

 

Theoretical Coverage

  • 5.7 m²/litre at 100 microns dft, allow appropriate loss factors

 

Method of Application

  • Airless Spray, Brush, Roller

 

Flash Point (Typical)

  • Part A 45°C
  • Part B 21°C
  • Mixed 38°C

 

Induction Period

  • Not required

 

Shelf Life

  • 12 months at 25°C. Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat and ignition.



Drying Information


-5°C 5°C 25°C 35°C
Touch Dry [ISO 9117/3:2010] 24 hours 12 hours 6 hours 4 hours
Hard Dry [ISO 9117-1:2009] 72 hours 24 hours 16 hours 12 hours
Pot Life 12 hours 8 hours 6 hours 4 hours



Overcoating Data


See limitations - click to jump to section

Substrate Temperature
-5°C 5°C 25°C 35°C
Intercept 7000 72 hours 14 days 24 hours 14 days 8 hours 7 days 5 hours 7 days
Intercept 8000 LPP 72 hours 14 days 24 hours 14 days 8 hours 7 days 5 hours 7 days
Intercept 8500 LPP 72 hours 14 days 24 hours 8 days 5 hours 7 days 5 hours 7 days
Intergard 263 - - 36 hours 42 days 8 hours 28 days 5 hours 14 days
Intergard 740 - - 36 hours 14 days 8 hours 14 days 5 hours 14 days
Intersheen 579 72 hours 5 days 36 hours 5 days 8 hours 5 days 5 hours 5 days
Intersleek 717 - - 36 hours ext 8 hours ext 5 hours ext
Intersmooth 7460HS SPC 72 hours 14 days 24 hours 8 days 8 hours 5 days 5 hours 3 days
Intersmooth 7465Si SPC 72 hours 14 days 24 hours 8 days 8 hours 5 days 5 hours 3 days
Intersmooth 7475Si SPC 72 hours 14 days 24 hours 8 days 8 hours 5 days 5 hrs 3 days
Interswift 6800HS 72 hours 7 days 24 hours 7 days 8 hours 7 days 5 hrs 7 days
Interswift 6900Si 72 hours 14 days 24 hours 8 days 8 hours 5 days 5 hrs 3 days
Interthane 990 72 hours 5 days 36 hours 5 days 8 hours 5 days 5 hrs 5 days
Intertuf 203 48 hours 15 days 24 hours 15 days 8 hours 15 days 5 hrs 15 days

In the overcoating data section 'ext' = extended overcoating period.

Note:

  • For Intersmooth 360, 365, 460, 465, 7370HS SPC, 7570 SPC and 7465HS SPC follow the overcoating interval data given for Intersmooth 7460HS SPC.
  • For Interspeed 6200 and 6400 follow the overcoating interval data given for Intersmooth 7460HS SPC.



Regulatory Data


VOC

  • 445 g/lt as supplied (EPA Method 24)
  • 306 g/kg of liquid paint as supplied. EU Solvent Emissions Directive (Council Directive 1999/13/EC)

Note: VOC values are typical and are provided for guidance purposes only. These may be subject to variation depending on factors such as differences in colour and normal manufacturing tolerances.



Certification


When used as part of an approved scheme, this product has the following certification:

When tested in accordance with ASTM D5108-96 (modified) Intergard 263 applied at a dry film thickness of 100 microns, forms a barrier to TBT leaching from an underlying TBT antifouling. Long term testing is ongoing.

Consult Rawlins Paints Technical for details on 0113 2455450 (option 2) or send a message to [email protected].



Systems & Compatibility


Consult our technical team on 0113 2455450 (option 2) or send a message to [email protected] for the system best suited for the surfaces to be protected.

Intergard 263 should only be applied over epoxy anticorrosive primers. The primer to be used will depend upon vessel area and application locations. Typical primers include:



Surface Preparations


Use in accordance with the standard Worldwide Marine Specifications.

All surfaces to be coated should be clean, dry and free from contamination.

High pressure fresh water wash or fresh water wash, as appropriate, and remove all oil or grease, soluble contaminants and other foreign matter in accordance with SSPC-SP1 solvent cleaning.

Intergard 263 should always be applied over a recommended primer coating system.

Intergard 263 should be used in accordance with the specification given by International Paint.

The primer surface should be dry and free of all contamination (oil, grease, salt etc.) and overcoated with Intergard 263 within the overcoating intervals specified. Consult the relevant primer data sheet.

Consult our technical team on 0113 2455450 (option 2) or send a message to [email protected] for specific recommendations.



Application


Mixing

Material is supplied in 2 containers as a unit. Always mix a complete unit in the proportions supplied.

  • Agitate base (Part A) with power agitator.
  • Combine entire contents of curing agent (Part B) with base (Part A) and mix thoroughly with power agitator.

 

Thinner

  • International GTA220. Thinning is not normally required.
  • Consult our technical team for advice during application in extreme conditions.
  • Do not thin more than allowed by local environmental legislation.

 

Airless Spray

  • Tip Range 0.46-0.66 mm (18-26 thou).
  • Total output fluid pressure at spray tip not less than 176 kg/cm² (2500 p.s.i.)

 

Conventional Spray

  • Application by conventional spray is not recommended.

 

Brush/Roller

  • Application by brush/roller is recommended for small areas only.
  • Multiple coats may be required to achieve specified film thickness.

 

Cleaner

 

Work Stoppages and Cleanup

Do not allow material to remain in hoses, gun or spray equipment. Thoroughly flush all equipment with International GTA220/GTA822 or International GTA415. Once units of paint have been mixed they should not be resealed and it is advised that after prolonged stoppages work recommences with freshly mixed units. Clean all equipment immediately after use with International GTA220/GTA822 or International GTA415. It is good working practice to periodically flush out spray equipment during the course of the working day. Frequency of cleaning will depend upon amount sprayed, temperature and elapsed time, including any delays. Do not exceed pot life limitations.

All surplus materials and empty containers should be disposed of in accordance with appropriate regional regulations/legislation.

 

Welding

In the event welding or flame cutting is performed on metal coated with this product, dust and fumes will be emitted which will require the use of appropriate personal protective equipment and adequate local exhaust ventilation.



Safety


All work involving the application and use of this product should be performed in compliance with all relevant national Health, Safety & Environmental standards and regulations.

Prior to use, obtain, consult and follow the Material Safety Data Sheet for this product concerning health and safety information. Read and follow all precautionary notices on the Material Safety Data Sheet (see the attachments section above) and container labels. If you do not fully understand these warnings and instructions or if you can not strictly comply with them, do not use this product. Proper ventilation and protective measures must be provided during application and drying to keep solvent vapour concentrations within safe limits and to protect against toxic or oxygen deficient hazards. Take precautions to avoid skin and eye contact (ie. gloves, goggles, face masks, barrier creams etc.) Actual safety measures are dependant on application methods and work environment.



Limitations


Spot Repair - The Intertuf 262/Intergard 263 system may be used for the spot repair of existing epoxy, coal tar epoxy, chlorinated rubber, vinyl tar and tar-free vinyl substrates. Feathered overlap areas must be kept to a minimum.

Consult Rawlins Technical. The Intertuf 262/Intergard 263 system is not suitable for repair of bituminous substrates. Upgrade - Intertuf 262/Intergard 263 may be used for the upgrade of existing epoxy, coal tar epoxy and chlorinated rubber substrates.

Substrates not suitable for upgrading:- vinyl tar, tar-free vinyl, bituminous.

Intergard 263 may be applied at substrate temperatures down to -15°C. Before applications are made below -5°C consult your local IP representative for further detail of application procedure.

Overcoating information is given for guidance only and is subject to regional variation depending upon local climate and environmental conditions. Consult your local International Paint representative/Rawlins for specific recommendations.

Apply in good weather. Temperature of the surface to be coated must be at least 3°C above the dew point. For optimum application properties bring the material to 21-27°C, unless specifically instructed otherwise, prior to mixing and application.

Unmixed material (in closed containers) should be maintained in protected storage in accordance with information given under "Shelf Life" in the Product Information section. Technical and application data herein is for the purpose of establishing a general guideline of the coating application procedures.

Test performance results were obtained in a controlled laboratory environment and International Paint makes no claim that the exhibited published test results, or any other tests, accurately represent results found in all field environments. As application, environmental and design factors can vary significantly, due care should be exercised in the selection, verification of performance and use of the coating.

 

Product Details
4810-775654

Data sheet

Manufacturer
International
For Use By
Professional Use
Interior / Exterior Use
Exterior Use
Application Method
Brush, Roller, Airless Spray
Sheen
Matt
Colour
Standard / Ready Mixed
Single, Two or Three Pack
Two-Pack
Pack Size
20L
Parts
2
Base Type
Epoxy
Interior/Exterior Use
Exterior
Solvent
Mixture - see safety data sheet
Mixing Ratio
4 volume(s) Part A to 1 volume(s) Part B
Suitable Substrates
Steel
Key Features
forms a barrier to TBT leaching from an underlying TBT antifouling, when used as part of an approved scheme.
Application
Brush, Roller, Spray
Coverage
5.7 m²/litre at 100 microns dft, allow appropriate loss factors
Recommended Thinner/Cleaner
International GTA220/GTA822 or International GTA415
Unit Contents
Base & curing agent
Compatible Topcoats
Intercept 7000, Intercept 8000 LPP, Intercept 8500 LPP Intergard 263; more in the product data sheet
Min. Application Temperature
may be applied at substrate temperatures down to -15°C. Before applications are made below -5°C consult International/Rawlins for further detail of application procedure.
Solids by Volume
57% ±2% (ISO 3233:1998)
VOC
445 g/lt as supplied (EPA Method 24) 306 g/kg of liquid paint as supplied. EU Solvent Emissions Directive (Council Directive 1999/13/EC
Shelf Life (from date of manufacture)
12 months at 25°C. Subject to re-inspection thereafter. Store in dry, shaded conditions away from sources of heat and ignition.
Touch Dry
6 hrs (at 25°C)
Finish
Matt
Size
20L
Recommended Dry Film Thickness
100 microns
Recommended Wet Film Thickness
175 microns
UN Number (Activator)
-
UN Number (Base)
UN1263
Pot Life
6 hours (at 25°C)
Dry to Recoat
5-8 hours min (at 25°C)
Hard Dry
16 hrs (at 25°C)
Base Type
Epoxy
Suitable For Use On
Epoxy Ant i-C orrosive Primers
Finish
Matt
Application Method
Brush
Application Method
Spray
Application Method
Roller
Product Usage Type
Tie Coat
Product Range
Intergard
Colour Family
Grey
Categorised As
Marine Paints > Antifouling Primers & Tie Coats
Seasonal
Cold Weather
Attachments
Download


Customer agrees that before placing an Order, Customer has read and understood the most up to date Product Data Sheet for the Product. Where we have access to the Product Data Sheet from the manufacturer, we will either provide a copy on request, or include a link to the Product Data Sheet available on the manufacturer’s website. Customer further agrees that we have no liability for any errors or omissions contained within the Product Data Sheets. For more information, please see our Terms & Conditions of Sale.


Be the first to ask a question about this product!


Question about the product

* Required fields
(read)
Send

IMPORTANT SHIPPING & DELIVERY INFORMATION

International Intergard 263 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.

Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.

Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.

All delivery costs below are excluding VAT


You might also like