560+ water based matt colours in a single pack topcoat for fire protection coatings. Specially designed for Firetex and Pyroplast intumescent fire protection systems against humidity and mechanical strain. Used as topcoat on fire protected structural steelwork and concrete for weathering and / or decorative reasons.
- Also known as Unitherm Top W
- Supplied ready for use
- No impact on the foaming reaction of intumescent coatings
- Free of halogens and aromatic solvents
- Complies with the highest sustainability requirements of DGNB (level 4) as part of the coating system
- Meets Type Z1 classification
- Minimum order quantity of 40 litres applies
Product customisation
Don't forget to save your customization to be able to add to cartFiretex Top WB (previously known as Sika Unitherm Top W) is a single pack topcoat specially designed for Firetex and Pyroplast intumescent fire protection systems against humidity and mechanical strain. The topcoat has no impact on the formation of the heat insulating foam of the intumescent coatings.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Recommended Use
- Technical Data
- Recommended Spreading Rate Per Coat
- Average Drying Times
- Surface Preparation
- Mixing
- Application Conditions
- Application Equipment
- Recommended Systems
Features & Benefits
- No impact on the foaming reaction of intumescent coatings
- 560+ RAL shades
- Individual coloration possible with corresponding topcoat, various colour shades in RAL, others available
- Free of halogens and aromatic solvents
- Meets Type Z1 classification (e.g. internal conditions include temperatures till + 5°C and high humidity) as part of the coating system
- Complies with the highest sustainability requirements of DGNB (level 4) as part of the coating system
Recommended Use
Used as topcoat on fire protected structural steelwork and concrete for weathering and / or decorative reasons.
In special conditions, e.g. frequent formation of condensation and / or heating up of surfaces above + 45°C, adequate arrangements should be taken. In dry and clean conditions, topcoating with Firetex Top WB on Firetex, Unitherm and Pyroplast fire protection coatings may not be required.
Technical Data
Volume Solids: | 40 ± 2 % |
Weight Solids: | 52 ± 2 % |
VOC: |
25 g/kg calculated from formulation to satisfy EC Solvent Emissions Directive (UK). |
Flash Point: | N/A |
Cleaner/Thinner: | Water (for cleaning) Thoroughly clean tools and equipment immediately after use. |
Pack Size: | Single component material: 11 kg (8.8 litre). Volume will vary with density. |
Density: | 1.25 kg/l (may vary with colours) |
Shelf Life: | 18 months from date of manufacture, stored in originally sealed containers in a cool and dry environment - Protect from frost. |
Recommended Application Methods: | Airless Spray, Brush and Roller |
Recommended Spreading Rate Per Coat
(Typical) | |
---|---|
Dry | 60 µm |
Wet | 115 µm |
Theoretical Consumption* |
0.144kg/m² 0.115 l/m² |
Theoretical Coverage* |
6.93 m²/kg 8.67 m²/l |
*This figure makes no allowance for surface profile, uneven application, overspray or losses in containers and equipment.
Due to an unleaded and unchromated pigment coating, a higher loading of 200 g/m² (0.160 l/m²) is required in several work steps to reach the designated opacity.
Average Drying Times
For 60 μm Dry Film Thickness:
20°C and 60% RH | |
---|---|
Dry to touch | 30 minutes |
Dry to handle | 6 hours |
To recoat | 6 hours |
A complete drying of the fire protection coating prior topcoat application is highly recommended.
Through-drying of the used Firetex, Unitherm or Pyroplast intumescent coating can be checked by ‘finger-nail-test’.
Final cure: Approx. 24 hours after application at + 20°C object temperature and 60 % relative humidity.
These figures are given as a guide only. Factors such as air movement, film thickness and humidity must also be considered.
Surface Preparation
Prior application of the topcoat, the surface to be coated must be dry, clean and free from dirt, oil, grease or any other contamination.
Mixing
The material is supplied ready for use; stir thoroughly with a mechanical paint mixer prior to application.
During mixing and handling of the materials always wear protective goggles, suitable gloves and other protective clothings.
Application Conditions
Substrate temperature shall be between + 5°C and + 40°C* and at least 3°C above the dew point.
Material temperature shall be above + 15°C
Relative air humidity shall be below 80%.
During application and drying of total Firetex, Unitherm or Pyroplast intumescent coating system including Firetex topcoats as well as transportation special protection measures must be taken against weathering.
Note: With critical situations e.g. frequent formation of condensation and / or heating up of surfaces above + 45°C, adequate arrangements should be taken.
* If higher temperatures occur, please consult Rawlins Technical on 0113 2455450 (option 2) or send a message to [email protected].
Application Equipment
The following is a guide. Changes in pressures and tip sizes may be needed for satisfactory application characteristics. Always purge spray equipment before use with listed cleaner (water).
Airless Spray
- Unit: Efficient airless equipment (pressure ratio > 30: 1)
- Tip Size: 0.28 – 0.38 mm (0.011 – 0.015 inch)
- Fan Angle: 40° - 80°
- Operating Pressure: min. 180 bar (2600 psi)
- Spray hoses: Ø ⅜ inch (10 mm), max. 20 m
- Ø ¼ inch (6 mm)
- Hoses must be used for water-based products only
Material shall be applied undiluted.
The airless spray details given above are intended as a guide only. Details such as fluid hose length and diameter, paint temperature and job shape and size all have an effect on the spray tip and operating pressure chosen. However, the operating pressure should be the lowest possible consistent satisfactory atomisation.
As conditions will vary from job to job, it is the applicators responsibility to ensure that the equipment in use has been set up to give the best results.
If in doubt consult Rawlins Technical on 0113 2455450 (option 2) or send a message to [email protected].
Brush and Roller
- Material shall be applied undiluted
- Load natural fine bristle brushes or short pile lambswool rollers are recommended
Recommended Systems
Steel
Surface and / or primer:
- See corresponding product data sheet of the Firetex, Unitherm or Pyroplast intumescent coating range
Intumescent coating:
- Firetex, Unitherm or Pyroplast intumescent coating for steel
Topcoat:
- Firetex Top WB
Galvanised steel
Interface:
- Macropoxy 2706 EG
Intumescent coating:
- Firetex, Unitherm or Pyroplast intumescent coating for steel
Topcoat:
- Firetex Top WB
IMPORTANT FIRE PRODUCTS NOTICE: The information displayed on this website should be used as a guide ONLY and our Technical Department should be contacted to obtain a tailored specification and any advice necessary before you place an order for fire protection products. Fire protection products are non-returnable except in accordance with Condition 8 of the Terms and Conditions and should be applied only by an individual with the necessary expertise and experience. We will not be held liable for any resulting damage to property, human life or monetary costs incurred due to the incorrect specification you have prepared or use of fire protection products caused by your negligence, including your failure to have contacted us to obtain the relevant advice/specification.
Data sheet
- For Use By
- Professional Use
- Interior / Exterior Use
- Interior & Exterior
- For Use On
- Steel
Galvanised Steel
Concrete
Structural Steelwork - Single, Two or Three Pack
- Single
- Application
- Brush, Roller, Spray
- Dry to Handle (at 20°C)
- 6 hours
- Dry to Recoat (at 20°C)
- 6 hours
- Fully Cured (at 20°C)
- Approx. 24 h after application at + 20°C object temperature and 60 % relative humidity.
- Coverage
- 8.67m²/l
- Recommended Thinner/Cleaner
- Water
- Max. Application Temperature
- 40°C
- Min. Application Temperature
- 5°C
- Density
- 1.25 kg/l
- Solids by Volume
- 40 ± 2 %
- VOC
- 25 g/kg
- Shelf Life (from date of manufacture)
- 18 months
- Touch Dry
- 30 minutes
- Size
- 11 kg (8.8 litre)
- Recommended Dry Film Thickness
- 60 µm
- Recommended Wet Film Thickness
- 115 µm
- Consumption
- 0.115 l/m²
- Solids by Weight
- 52 ± 2 %
- Base Type
- Water-Based
- Suitable For Use On
- Concrete
- Suitable For Use On
- Steel
- Suitable For Use On
- Galvanised Steel
- Suitable For Use On
- Structural Steelwork
- Application Method
- Brush
- Application Method
- Roller
- Application Method
- Spray
- Components
- 1K
- Usages
- Fire Resistance
- Product Usage Type
- Topcoat
- Product Range
- Firetex
- Colour Family
- Off-White
- Colour Family
- Black
- Colour Family
- Magnolia
- Colour Family
- White
- Colour Family
- Anthracite Grey
- Colour Family
- Neutral
- Colour Family
- Cream
- Colour Family
- Violet
- Colour Family
- Beige
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Colour Family
- Pink
- Colour Family
- Orange
- Colour Family
- Purple
- Colour Family
- Yellow
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Sherwin-Williams Firetex Top WB is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT