Tor HB Micaceous Iron Oxide, a high build anti-corrosive coating for structural steelwork on structures such as cranes, bridges, gantries, tanks, etc.
- Apply by spray or brush
- Brush application will only achieve 45 to 70 microns dry film thickness
- 2 colours available
- Touch dry in 2 hours
- Overcoat after 16 hours
- Micaceous oxide of iron pigment in a modified alkyd binder and thinned with low aromatic white spirit for application
- Use Tor TH10 if thinning required
Tor HB Micaceous Iron Oxide applies to structural steelwork for protection against corrosion, on structures such as:
- Cranes
- Transmission towers
- Bridges
- Gantries
- Tanks
- And many more
The high build coating is applied by airless spray (see below for details) or brush, though brush application will only achieve 45 to 70 microns dry film thickness, and requires approx. 16 hours to dry before overcoating (at 20°C). Steel surfaces should be suitably prepared and primed with Tor QD HB Phosphate Primer (AK636) or Tor HB Phosphate Primer (AK623).
Features & Benefits
- Corrosion protection on structural steelwork
- Ideal for structures such as cranes, bridges, tanks
- Apply by spray or brush
- Brush application will only achieve 45 to 70 microns dry film thickness
- Touch dry in 2 hours
- Overcoat after 16 hours
- Use Tor TH10 if thinning required
Product Information
Micaceous oxide of iron pigment in a modified alkyd binder and thinned with low aromatic white spirit for application.
Product reference | AK753 |
Volume solids | 45% |
Typical thickness | 45 to 100 microns dft from 90 to 200 microns wet |
Theoretical coverage | 5 to 10 square metres per litre |
Practical coverage | Reduce by up to 20% |
VOC content | EU limit value for this product (cat A/i): 500 g/l . This product contains max 500 g/l VOC |
Surface Preparation
Apply to steel which has been suitably prepared and primed with Tor QD HB Phosphate Primer (AK636) or Tor HB Phosphate Primer (AK623).
Application Details
Mix ratio | N/A |
Method of application | Brush or airless spray (will require reduction with 10% Tor TH10 for airless spray) (tip size 0.019”-0.021” and 2000 psi atomising pressure). |
Thinner | Tor TH10 (when required) |
Cleaner | Tor TH10 (for cleaning equipment) |
Pot Life | N/A |
Drying Times
Substrate Temperature | Touch Dry | Hard Dry | Overcoating Interval | |
---|---|---|---|---|
Minimum | Maximum | |||
20°C | 2 hours | 16 hours | 16 hours | 28 days |
Note: Drying/curing times will be shortened by higher temperatures and lengthened by lower temperatures
Storage and Handling
Store in a safe place out of the reach of children
Flash point
- 36°C
Shelf life
- 2 years in unopened containers
Limitations
Brush application will only achieve 45 to 70 microns dry film thickness
- Avoid skin and eye contact i.e. wear gloves, goggles, etc
- Ensure good ventilation, mechanical if necessary
- Store and use away from heat and flame
- Do not eat or smoke in the vicinity of work
- Wash hands before eating
- Refer to supply container for additional warning labels
Data sheet
- Manufacturer
- Tor Coatings
- For Use By
- Professional Use
- Water / Solvent Based
- Solvent
- For Use On
- Steel
- Application Method
- Brush, spray
- Sheen
- Matt
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Single
- Pack Size
- 5L
- Parts
- 1
- Solvent
- Micaceous oxide of iron pigment in a modified alkyd binder and thinned with low aromatic white spirit for application.
- Mixing Ratio
- -
- Key Features
- Protects structural steel from corrosion
- Touch Dry (at 20°C)
- 2 hours
- Dry to Handle (at 20°C)
- -
- Dry to Recoat (at 20°C)
- 16 hours
- Fully Cured (at 20°C)
- 16 hours
- Pot Life (at 20°C)
- -
- Coverage
- 5 to 10 square metres per litre
- Recommended Thinner/Cleaner
- Tor TH10
- Unit Contents
- -
- Compatible Primers
- Tor QD HB Phosphate Primer (AK636) or Tor HB Phosphate Primer (AK623)
- Compatible Topcoats
- -
- Max. Application Temperature
- -
- Min. Application Temperature
- -
- Density
- -
- Solids by Volume
- 45%
- Heat Resistance (up-to)
- -
- VOC
- This product contains max 500 g/l VOC
- Shelf Life (from date of manufacture)
- 2 years in unopened containers
- UN Number
- UN1263
- Base Type
- Solvent-Based
- Suitable For Use On
- Steel
- Finish
- Matt
- Application Method
- Brush
- Application Method
- Spray
- Usages
- MIO
- Product Usage Type
- Topcoat
- Product Range
- Tor Industrial
- Colour Family
- Neutral
- Colour Family
- Silver
- Dry to Recoat (@ 20-25°C)
- 16 hours
Questions
Question about the product
Donna Cox on 2022-07-11 18:09:01 | Question:
Is this product suitable for painting old iron guttering on houses? Is the silver colour a very bright silver or dull silver? Thank you! |
Answer from Rawlins’ Technical Team:
Unfortunately no, assuming the iron gutters are bare, clean, dry, sound and prepared as detailed in the technical data sheet we can recommend Rust-Oleum 3369/3380 CombiPrimer Anti-Corrosion followed by Rust-Oleum CombiColor Original. This is available in many RAL, NCS or BS colours in a satin or gloss finish. | |
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tor HB Micaceous Iron Oxide is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tor General Purpose Thinner
Tor General Purpose Thinner (TH10) - also known as Tor Tortread SP Thinners - is to be used for the thinning (where necessary) of general purpose primers, undercoats and finishes or for cleaning the same materials from brushes, rollers and trays immediately after application.
Tor QD High Build Phosphate Primer
Tor QD High Build Phosphate Primer, a quick drying high build anti-corrosive primer for blast cleaned or mechanically cleaned mild steel. Applied by spraying, the primer is touch dry in 1 hour and hard dry in 4 hours. Anti-corrosion protection for cleaned mild steel An alkyd resin binder with zinc phosphate anti-corrosive pigment, together...
Tor Hi Build Zinc Phosphate Primer
A single pack high build primer for blast/manually cleaned steel. An excellent lead and chromate-free anticorrosive. Protective primer for steel A urethane alkyd binder with zinc phosphate anti-corrosive, together with inert inorganic pigments and thinned with low aromatic white spirit Good coverage - 6.45 square metres per litre Applies...
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...