Self-smoothing epoxy resin seamless floor finish with non-dusting aggregates, designed to provide a flat hard wearing gloss finish ideal for industrial use, following the profile of the existing floor with aesthetically pleasing results and good chemical resistance and durability.
- Three part (Base, Hardener & Aggregate)
- Seamless and Hygienic
- Silica free
- Ease of application
- Dry for light traffic in 24 hours
- Excellent abrasion and impact resistance, with good chemical resistance
- Smooth finish for precise operation equipment
- Recommended uses include in pharmaceutical production, printing and packaging areas, television studios, automotive production, domestic studios, industrial workshops, medical and healthcare
- Formerly known as Resuflor VF
- More colours - with minimum order quantities and longer lead times - are available on RSL Resuflor SL X - Special Colours
Resuflor SL X (formerly known as Resuflor VF) is a self-smoothing epoxy resin seamless floor finish with low VOC content, with non dusting aggregates designed to provide a flat hard wearing gloss finish 2-3 mm in thickness following the profile of the existing floor. The system gives aesthetically pleasing results with good chemical resistance and durability, ideal for industrial use.
Features & Benefits
- Epoxy resin floor finish
- Seamless
- Silica free
- Low VOC
- Provides a hard wearing durable floor for industrial use
- Ease of application
- Hygienic
- Excellent abrasion and impact resistance
- Good chemical resistance
- Smooth finish for precise operation equipment
- Recommended uses include:
- Pharmaceutical production
- Printing and packaging areas
- Television studios
- Automotive production
- Domestic studios
- Industrial workshops
- Medical and healthcare
- See below for product data and application information
Products required for this system
- Primer : Resuprime NT or R.S. Dampshield on damp surfaces, where required.
- System : Resuflor SL X
- Optional Finish Coat: Resupen WB Clear Matt for a matt finish
Information & Data | |
---|---|
Product Information | |
Finish | Smooth Gloss |
Recommended thickness range | 2-3mm |
Solids Content by Weight | 100% |
Pack Make Up | 1 x Base 1 x Hardener 1 x Filler SL1 Aggregate |
Shelf Life | 12 months (Base, Hardener & Aggregate) |
Storage | Keep out of direct sunlight. Store in a dry place, between 15°C and 30°C. |
Application Information (at 20°C) | |
Coverage Rate (Theoretical) | 29.5kg will cover 7.8m² at 2mm thickness or 5.2m² at 3mm thickness |
* Coverage rate is calculated based on a sealed and smooth surface and may vary based on the substrate roughness and other conditions. | |
Pot Life | 25-30 Minutes |
Recoating Intervals | 12-16 hours |
Light Traffic | 24 hours |
Full Traffic | 72 hours |
Full Chemical Cure | 7 days |
Technical Information | |
The following figures are obtained from laboratory tests and RSL's experience with this product. | |
Slip Resistance (Method BS7976-1 + A1 2013, Method BS7976-2 + A1 2013, Method BS7976-3 + A1 2013) | Dry > 60 |
Wet (Please consult Sherwin-Williams/Rawlins Paints Technical) | |
The slip resistance of a floor surface can vary as a result of the installation process, conditions at the time of application and subsequent traffic. Inappropriate cleaning or maintenance can adversely affect the performance. For further advice on potential wet areas please consult Sherwin-Williams. | |
Abrasion Resistance (BS EN 13892-4:2002) | AR 0.5 (< 50 microns wear) |
Shore D Hardness ( BS EN ISO 868:2003) | 85 |
Tensile Strength ( BS EN ISO 527-2:2012) | 20 N/mm² |
Flexural Strength (BS EN ISO 178 +A1:2013) | 45 N/mm² |
Bond Strength ( BS EN 13892-8:2002) | >3 N (Substrate failure) |
Temperature Resistance | Tolerant of temperatures up to 60°c |
Chemical Resistance | Good Chemical Resistance - Consult Sherwin-Williams/Rawlins Technical on specific materials |
VOC | 81 g/l Calculated per full mixed unit |
Life Expectancy | 3-5 years depending on applied thickness and subjected to traffic according to FeRFA classification. Sherwin-Williams terms and conditions will apply. |
Preparation
New Concrete Floors:
New concrete must be clean, sound, dry, fully cured and surface laitance removed by vacuum enclosed shot blasting or mechanical grinding, a minimum strength of 25N/mm² is required.
Existing Concrete Floors:
Remove all dirt, oil, grease, old paint or any other surface contaminants by vacuum enclosed shot blasting, scarifying or mechanical grinding. Fats, oils or greases must be removed by mechanical means and detergent washing and make sure all residue of detergent is washed and removed by rinsing with clean water. Local repairs should be carried out using Resupatch.
Existing Floors ( previously coated )
All previous coatings and loose floor paints must be removed by mechanical preparation as described in the above section and primed as specified. if the old resin flooring cannot be removed, then please consult with our technical team for advice on intercoat adhesion and suitability, as it may not be compatible with existing floor coating.
Priming
Open and porous substrates will require priming with Resuprime NT on dry substrates only with less than 75% ERH reading.
Where the Relative Humidity of a substrate exceeds 75% ERH Resuprime MVT should be specified and selected on the basis of hygrometer readings in accordance with BS 8203:2017. The number of coats to be applied is chosen in accordance with the following table.
ERH % | Required Coating Thickness |
---|---|
75-85 | 1 coat of Resuprime MVT at 200 microns per coat |
85-92 | 2 coats of Resuprime MVT at 200 microns per coat |
92-97 | 3 coats of Resuprime MVT at 200 microns per coat |
For Further information please refer to recommended individual product data sheets.
Application
The ambient temperatures of the areas should not be allowed to fall below 15°C throughout the application and the curing period, as this could have an adverse effect on the appearance and colour of the system. Surface temperature must be above 10°C. Where possible it is recommended that the application area is heated to a minimum temperature of 15°C ideally to allow the ambient and substrate temperature to stabilise prior to installation.
Mixing:
Pre-mix the coloured component (base) to a uniform colour, then mix the entire contents of base with the hardener. If a separate mixing bucket is being used ensure all contents of both components are removed from the buckets supplied. Mix using a slow speed electric mixer for approximately one to two minutes until the two components have fully combined then add the aggregate slowly. Mix for a further 1-2 minutes until the aggregate has fully combined and there are no lumps. The mixed unit should be applied immediately.
Resuflor SL X should be worked with a trowel or float to achieve an even smooth finish. This is best achieved by the application of smooth even pressure with the compound poured over the correct coverage rate after fixing the stop ends to control the flow of the material. Then roll the area with a spiked roller to achieve an even smooth surface and remove entrapped air. Do not re-roll the area later than 10-15 mins.
The surface should be protected from temperatures of less than 10°C and moisture in the early stages of cure. This could adversely affect the flow, levelling and surface finish of Resuflor SL X.
Maintenance and Cleaning
Resuflor SL X should be cleaned with a regular industrial cleaning regime, after specified full chemical cure time limit, with a floor scrubber utilising R.S. Industrial Floor Cleaner or similar with dirty water being removed. Isolated localised cleaning can be carried out using R.S. Tyre Mark Remover, R.S. Fats, Oils & Grease Remover & R.S. Oil Remover.
All surfaces should be thoroughly rinsed with clean water after the use of chemical cleaners.
Please refer to the RSL Guide to Cleaning of Resin Floors
Data sheet
- For Use By
- Industrial Use
- Interior / Exterior Use
- Interior Use
- Water / Solvent Based
- Solvent
- For Use On
- Concrete Floors
- Application Method
- Brush
Roller
Squeegee - VOC Levels
- Low (50-149 g/l)
- Single, Two or Three Pack
- Three-Pack
- Pack Size
- 29.5KG
- Solvent
- Epoxy
- Mixing Ratio
- -
- Key Features
- Chemical resistant, heavy duty, ideal for industrial use
- Dry to Recoat (at 20°C)
- 12-16 hours
- Fully Cured (at 20°C)
- 7 days
- Pot Life (at 20°C)
- 25-30 Minutes
- Coverage
- 29.5kg will cover 7.8m² at 2mm thickness or 5.2m² at 3mm thickness
- Recommended Thinner/Cleaner
- R.S. Industrial Floor Cleaner
- Unit Contents
- 1 x Base 1 x Hardener 1 x Filler SL1 Aggregate
- Compatible Primers
- Resuprime NT, Resuprime MVT
- Compatible Topcoats
- Resupen WB Clear Matt
- Max. Application Temperature
- -
- Min. Application Temperature
- 15°C
- Density
- -
- Solids by Volume
- -
- Heat Resistance (up-to)
- -
- VOC
- 81 g/l Calculated per full mixed unit
- Shelf Life (from date of manufacture)
- 12 months (Base, Hardener & Aggregate)
- UN Number
- UN3082, UN3066
- UN Number (Activator)
- UN3066
- UN Number (Base)
- UN3082
- Dry for Light Traffic (at 20°C)
- 24 hours
- Dry for Full Traffic (at 20°C)
- 72 hours
- Suitable For Use On
- Concrete Floors
- Finish
- Smooth Gloss
- Application Method
- Brush
- Application Method
- Roller
- Application Method
- Squeegee
- Components
- 3K
- Product Usage Type
- Self Smoothing Screed
- Product Range
- Resuflor
- Colour Family
- Grey
- Average Application Thickness
- 2-3mm
- Product Type
- Epoxy
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
RSL Resuflor SL X - Standard Readily Available Colours is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT