Tikkurila Duasolid 50, a two-component, high-solids oxirane ester paint containing active anti-corrosive pigments. This eco-friendly alternative to epoxy and polyurethane paints is suitable for earth moving machines, haulage and lifting equipment, forklifts, agricultural machinery, electric appliances, pumps and other steel structures, equipment and machinery.
- Huge colour range from RAL, BS & NCS
- Iso-cyanate free DTM product - The paint offers quality similar to that achieved with polyurethanes
- Good corrosion resistance - Does not compromise protection or performance
- Can be applied in thick layers (up to 100 µm / one coat), thus enabling faster production
- An ideal option for OEM
- For industrial and professional use only.
Product customisation
Don't forget to save your customization to be able to add to cartTikkurila Duasolid 50 is a two-component, high-solids oxirane ester paint containing active anti-corrosive pigments, an eco-friendly alternative to epoxy and polyurethane paints.
Duasolid 50 is an option when products containing iso-cyanate cannot be used, offering quality similar to that achieved with polyurethanes. Laboratory and field testing have proved the effectiveness of Duasolid systems in providing excellent corrosion protection, both for interior and exterior service environments.
Duasolid 50 has a high solids content and can be applied in thick layers, thus enabling faster production. The product is an ideal option for OEM and other steel structures, equipment and machinery.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoat
- Application Conditions
- Mixing Components
- Application
- Thinner/Cleaner
- VOC
- Health And Safety
Features & Benefits
- Huge colour range from RAL, BS & NCS
- An option when products containing iso-cyanate cannot be used
- Offers quality similar to that achieved with polyurethanes
- Does not compromise protection or performance. Laboratory and field testing have proved the effectiveness of Duasolid systems in providing excellent corrosion protection, both for interior and exterior service environments
- A high solids content and can be applied in thick layers, thus enabling faster production
- Used as a single coat or as a topcoat in oxirane-ester based systems on steel surfaces exposed to abrasion and chemicals in severe climatic conditions
- For interior and exterior service environments
- High film-building properties, up to 100 µm / one coat
- Resistance to continuous temperature up to +80°C dry heat and temporarily up to +120°C dry heat
- Suitable for steel structures, equipment and machinery including, but not exhausted to:
- Earth moving machines
- Haulage and lifting equipment
- Forklifts
- Agricultural machinery
- Electric appliances
- Pumps
Technical Data
- Volume Solids: approx. 65±2%
- Weight Solids: 77±2%
- Specific Gravity: approx. 1.5 kg / l
- Mixing Ratio:
- Base - 2 parts by volume (Duasolid 50)
- Hardener - 1 part by volume (008 7675)
- Pot Life (+23°C): 8 hours
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
95µm | 60µm | 10.8 m²/l |
160µm | 100µm | 6.5 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 80 µm | 23°C |
---|---|
Dust dry, after | 30-60 min |
Touch dry, after | 4-6 h |
Dry to handle, after | 8-12 h |
Recoatable with other Duasolid 50 paints, after | a few min |
Through dry at increased temperature after 45min / +80ºC |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation
Surface Preparation
Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces: Blast clean to grade Sa2½. (ISO 8501-1) If blast cleaning is not possible, phosphating is recommended for cold rolled steel to improve adhesion.
Primed surfaces: Oil, grease, salt and dirt are removed from the surface by appropriate means. Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Recommended Primers
Temanyl PVB, Duasolid 50.
Recommended Topcoat
Duasolid 50.
Application Conditions
- All surfaces must be clean, dry and free from contamination.
- The temperature of the ambient air, surface and paint should not fall below +10ºC during application and drying.
- Relative humidity of the air should not exceed 80% during application and drying.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- For airless spraying, the product is thinned approximately 0–15% to the viscosity 30–60s (DIN4). Recommended nozzle tip is 0.011"–0.017", pressure ratio at least 30:1 and pressure 120–200 bar. Spray angle shall be chosen according to the shape of the object.
- For conventional spraying, the product is thinned approximately 10–15% to the viscosity 20–40s (DIN4). Recommended nozzle tip is 1,6–1,8 mm and pressure 2–4 bar.
- For electrostatic spraying, the product is thinned approximately 10–15% to the viscosity 20–40s (DIN4). Recommended nozzle tip is 0.011"–0.013" and pressure 120–140 bar. Spray angle shall be chosen according to the shape of the object.
Properties and gloss of Duasolid 50 will vary according to the used hardener:
- Hardener 008 7675 (supplied) - gloss abt. > 70 - mixing ratio 2:1
The following hardeners have different gloss grades and can be requested, with extended lead times:
- Hardener 008 7665 - gloss abt. 60 - mixing ratio 2:1
- Hardener 008 7667 - gloss abt. 10 - mixing ratio 2:1
- Hardener 008 7672 - gloss abt. 40 - mixing ratio 2:1
Please contact Rawlins Paints' Sales Support Team on 0113 2455450 or send a message to [email protected] for more information.
Avoid hot spray!
Thinner/Cleaner
VOC
The Volatile Organic Compounds amount is 320 g/litre of paint mixture. VOC content of the paint mixture (thinned 15% by volume) is 399 g/l.
Health And Safety
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial and professional use only.
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Data sheet
- Manufacturer
- Tikkurila
- Interior / Exterior Use
- Interior & Exterior
- For Use On
- Steel
- Application Method
- Spray
- Sheen
- Gloss
- Colour
- Fully Tintable
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 10L
- Parts
- Two
- Interior/Exterior Use
- Both
- Solvent
- Mixture (see Safety Data Sheet)
- Suitable Substrates
- Metal
- Touch Dry (at 20°C)
- 6 hours
- Coverage
- 6.5 m²/l - 10.8 m²/l
- Recommended Thinner/Cleaner
- Thinner 1048, Thinner 1112
- Compatible Primers
- Duasolid Primer, Temanyl PVB, Duasolid 50
- Compatible Topcoats
- Duasolid 50
- Min. Application Temperature
- 10ºC
- Solids by Volume
- approx. 65±2%
- VOC
- 320 g/litre
- Finish
- Gloss
- Recommended Dry Film Thickness
- 60µm -100µm
- Recommended Wet Film Thickness
- 95µm - 160µm
- UN Number (Activator)
- UN1263
- UN Number (Base)
- UN1263
- Dry to Recoat (at 23°C)
- A few minutes (see TDS)
- Touch Dry (at 23°C)
- 4-6 hours
- Dry to Handle (at 23°C)
- 8-12 hours
- Pot Life
- 8 hrs
- Base Type
- Solvent-Based
- Suitable For Use On
- Steel
- Suitable For Use On
- Primed Surfaces
- Finish
- Gloss
- Application Method
- Spray
- Usages
- 1 Coat
- Usages
- Exterior Durability
- Usages
- Heat Resistance
- Usages
- Severe Exposures
- Usages
- Direct to Metal
- Usages
- High Solids
- Usages
- Chemical Resistance
- Usages
- High Build
- Usages
- Abrasion Resistant
- Usages
- Corrosion Resistance
- Usages
- Atmospheric
- Usages
- Anti-Corrosive
- Product Usage Type
- Topcoat
- Product Range
- Duasolid
- Colour Family
- Yellow
- Colour Family
- Black
- Colour Family
- White
- Colour Family
- Neutral
- Colour Family
- Anthracite Grey
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Colour Family
- Pink
- Colour Family
- Orange
- Colour Family
- Purple
- Product Type
- Oxirane Ester
- Environment
- Atmospheric
- Environment
- Exterior Durability
- Environment
- Severe Exposures
- Touch Dry/Dust Free (@ 20-25°C)
- 6 hours
- Product Attributes
- 1 coat
- Product Attributes
- High Build
- Product Attributes
- High Solids
- Product Attributes
- Anti-Corrosive
- Resistance to
- Heat
- Resistance to
- Corrosion
- Resistance to
- Abrasion
- Resistance to
- Chemicals
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Duasolid 50 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT