Temacoat GPL, a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Due to CE marking it is also suitable for concrete surfaces in process industries.
- Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
- Resists +150°C dry heat and chemically active gases and dust
- Withstands well immersion in water, oil and dilute solutions of non-oxidizing acids, alkalis and salts
- Withstands immersion in mineral/vegetable/animal fats and oils
- Available in a wide range of RAL & BS colours
Product customisation
Don't forget to save your customization to be able to add to cartTemacoat GPL is a two-component, amine adduct cured mar and chemical resistant epoxy topcoat used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack. Resists+150°C dry heat and chemically active gases and dust and, due to CE marking, it is also suitable for concrete surfaces in process industries.
Temacoat GPL withstands well immersion in water (+60ºC), oil and dilute solutions of non-oxidizing acids, alkalis and salts, with resistance to abrasion and chemicals making the surface retain its colour for a longer time
Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
For industrial use only.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Primers
- Recommended Topcoats
- Application Conditions
- Mixing Components
- Application
- Thinners & Cleaners
Features & Benefits
- Used especially as a finishing coat especially for objects exposed to heavy abrasion and chemical attack.
- Resists +150°C dry heat and chemically active gases and dust
- Due to CE marking also suitable for concrete surfaces in process industries
- Withstands well immersion in water, oil and dilute solutions of non-oxidizing acids, alkalis and salts
- Wide colour range
- Resistance to abrasion and chemicals makes the surface retain its colour for a longer time
- Withstands +60ºC in immersion
- Resists only temporary splashes of oxidizing acids and bleaching solutions
- Withstands immersion in mineral/vegetable/animal fats and oils
- Recommended for bridges, tanks and different types of steelwork and equipment in the wood processing and chemical industries, such as tubular bridges, conveyors, paper machines etc
Technical Data
- Volume solids: 55±2% (ISO 3233)
- Weight solids: 69±2%
- Specific gravity: 1.3–1.4 kg / l (mixed) depending on colour
- Pot life: 5 hours
- VOC:
- The Volatile Organic Compounds amount is 450 g/litre of paint mixture
- VOC content of the paint mixture (thinned 10% by volume) is 490 g/l
- Mixing ratio:
- Base 3 parts by volume Temacoat GPL
- Hardener 1 part by volume 008 7580
Recommended Film Thicknesses and Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
90µm | 50µm | 11.0 m²/l |
185µm | 100µm | 5.5 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 60µm | 10°C | 23°C | 35°C |
---|---|---|---|
Dust dry, after | 3h | 2h | 1h |
Touch dry, after | 10h | 5h | 2h |
Recoatable, after | 10h | 4h | 2h |
Recoatable in immersion, after | 32h | 16h | 8h |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
Primed surfaces:
- Oil, grease, salt and dirt are removed from the surface by appropriate means.
- Repair any damage to the primer coat. Note the overcoating time of primer. (ISO 12944-4)
Concrete surfaces:
- The surface must be dry and at least 4 weeks old.
- The relative humidity of the concrete should not exceed 97%.
- Remove any splashes and unevennesses by grinding.
- Remove laitance and form oil from concrete castings by sanding or blast cleaning.
- Any cracks, crevices and voids must be repaired with a mixture of Temafloor 200 and fine dry quartz sand.
Recommended Primers
- Temacoat GPL-S Primer
- Temacoat GPL-S MIO
- Temacoat SPA Primer
- Temabond ST 200
- Temabond ST 300
- Temacoat Primer
Recommended Topcoats
- Temacoat GPL
Application Conditions
- All surfaces must be clean, dry and free from contamination.
- The temperature of the ambient air, surface and paint should not fall below +10ºC during application and drying.
- Relative humidity of the air should not exceed 80% during application and drying.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolor or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use. Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- For airless spraying, the product is thinned approximately 0–10%.
- Recommended nozzle tip is 0.011"–0.017" and pressure 120–160 bar.
- Spray angle shall be chosen according to the shape of the object.
- For brush application product should be thinned according to the circumstances.
Thinners & Cleaners
Thinner 1031
Data sheet
- Manufacturer
- Tikkurila
- For Use By
- Consumer Use
- For Use On
- Steel, Concrete
- Application Method
- Brush, Spray
- Sheen
- Gloss
- Colour
- Fully Tintable
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 10L
- Parts
- 2 component
- Base Type
- Epoxy
- Minimum Applied Thickness
- 50µm (dry), 90µm (wet)
- Maximum Applied Thickness
- 100µm (dry), 185µm (wet)
- Solvent
- Mixture - see safety sheet
- Mixing Ratio
- Base 3 parts by volume - Hardener 1 part by volume
- Suitable Substrates
- Steel, concrete
- Key Features
- Topcoat for objects exposed to heavy abrasion and chemical attack
- Application
- Brush, Spray
- Touch Dry (at 20°C)
- 5 hours
- Pot Life (at 20°C)
- 5 hours
- Coverage
- 5.5 m²/l - 11.0 m²/l
- Recommended Thinner/Cleaner
- Thinner 1031
- Unit Contents
- Base, hardener
- Compatible Primers
- Temacoat GPL-S Primer, Temacoat GPL-S MIO, Temacoat SPA Primer, Temabond ST 200, Temabond ST 300, Temacoat Primer.
- Compatible Topcoats
- Temacoat GPL
- Solids by Volume
- 55±2% (ISO 3233)
- VOC
- VOC content of the paint mixture (thinned 10% by volume) is 490 g/l
- Recommended Dry Film Thickness
- 50µm - 100µm
- Recommended Wet Film Thickness
- 90µm - 185µm
- UN Number (Activator)
- UN1263
- UN Number (Base)
- UN1263
- Dry to Recoat (at 10°C)
- 10h
- Touch Dry (at 10°C)
- 10h
- Dry to Recoat (at 23°C)
- 4h
- Touch Dry (at 23°C)
- 5h
- Base Type
- Solvent-Based
- Suitable For Use On
- Concrete
- Suitable For Use On
- Steel
- Suitable For Use On
- Primed Surfaces
- Finish
- Gloss
- Application Method
- Brush
- Application Method
- Spray
- Usages
- Abrasion Resistant
- Usages
- Atmospheric
- Usages
- Immersion
- Usages
- Mineral Oil Resistance
- Usages
- Mar Resistance
- Usages
- Animal & Vegetable Oils Resistance
- Usages
- Heat Resistance
- Usages
- Chemical Resistance
- Product Usage Type
- Topcoat
- Product Range
- Temacoat
- Colour Family
- Pink
- Colour Family
- Orange
- Colour Family
- Purple
- Colour Family
- Yellow
- Colour Family
- Black
- Colour Family
- White
- Colour Family
- Anthracite Grey
- Colour Family
- Beige
- Colour Family
- Grey
- Colour Family
- Green
- Colour Family
- Blue
- Colour Family
- Red
- Colour Family
- Brown
- Product Type
- Alkyd
- Environment
- Immersion
- Environment
- Atmospheric
- Touch Dry/Dust Free (@ 20-25°C)
- 5 hours
- Product Attributes
- Gloss Retention
- Product Attributes
- Colour Retention
- Product Attributes
- Tough / Durable
- Resistance to
- Mineral Oil
- Resistance to
- Animal & Vegetable Oils
- Resistance to
- Mar
- Resistance to
- Abrasion
- Resistance to
- Chemicals
- Resistance to
- Heat
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temacoat GPL is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Temabond ST 200
2 component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications. Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions than conventional epoxy paints....
Tikkurila Temabond ST 300
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation. Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temacoat GPL-S MIO
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments Fast cure and low-temperature cure hardeners available - click to...
Tikkurila Temacoat GPL-S Primer
Tikkurila Temacoat GPL-S Primer is a two-component, polyamide-cured high build epoxy primer containing zinc phosphate. Excellent adhesion to steel, zinc and aluminium surfaces. Used as a primer or an intermediate coat in paint systems exposed to abrasion and chemical stress. Can be overcoated after a prolonged period of time. Faster...
Tikkurila Temacoat Primer
A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress. Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment Adheres well to...
Tikkurila Temacoat SPA Primer
Tikkurila Temacoat SPA Primer, a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces, that can be applied in thick layers, thus enabling faster production. Has high solids content Used as a primer or an intermediate coat in paint systems exposed to abrasion...
Tikkurila Thinner 1031
Tikkurila Thinner 1031 is a thinner for epoxy paints, silicone paints, polyvinylbutyral paints, 2-component zinc rich paints and epoxy shop primers.
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...