Solvent-free, elastic two-component polyurethane coating.
- For new and old concrete and asphalt floors exposed to mechanical and chemical stress.
- Withstands water, oils, greases, chemicals and dilute solutions of non-oxidizing acids, alkali and salt solutions. Resists only temporary splashes of oxidizing acids and bleaching chemicals.
- Withstands +80ºC dry heat. Does not resist abrupt changes of temperature.
- Good impact resistance.
- Self-levelling, to be applied with serrated or steel trowel.
- Recommended for industrial and storage facilities, repair shops; e.g. air handling units, process or paper machine units and corridors.
Professional use only - from the 24th August 2023, adequate training is required before industrial or professional use of this product.
Should you require training, visit - https://www.safeusediisocyanates.eu/
Professional use only - from the 24th August 2023, adequate training is required before industrial or professional use of this product.
Should you require training, visit - https://www.safeusediisocyanates.eu/
Tikkurila Temafloor PU is a solvent-free, elastic two-component polyurethane coating. It withstands mechanical and chemical stresses in industrial and storage facilities, etc.
Temafloor PU can be used for new and old concrete as well as for asphalt floors. This is a tintable paint and it can be tint in many colors.
It has good resistance to abrasion and withcstands chemicals and heat. The coating forms a durable, seamless and easy-to-clean surface. Temafloor PU does not shrink or crack.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Surface Preparation
- Recommended Topcoats
- Application Conditions
- Mixing Components
- Application
- VOC
- Health And Safety
Features & Benefits
- Good resistance to abrasion
- Elongation value approx. 60%
- Withstands water, oils, greases, chemicals and dilute solutions of non-oxidizing acids, alkali and salt solutions. Resists only temporary splashes of oxidizing acids and bleaching chemicals
- Withstands +80ºC dry heat. Does not resist abrupt changes of temperature
- Good impact resistance
- Self-levelling, to be applied with serrated or steel trowel
- Recommended for industrial and storage facilities, repair shops; e.g. air handling units, process or paper machine units and corridors
Technical Data
Technical Data | ||||||
---|---|---|---|---|---|---|
Tikkurila Temafloor PU | ||||||
Volume Solids: | approx. 100% | |||||
SG: | 1.4 kg / litre (mixture) | |||||
Viscosity: | n/a | |||||
Density: | 1.4 g/cm³ - Hardener: 1,23 g/cm³ | |||||
Storage Conditions: | Store away from direct sunlight in a dry, cool and well-ventilated area, away from incompatible materials (see Section 10). Keep container tightly closed. Containers that have been opened must be carefully resealed and kept upright to prevent leakage. Do not store in unlabeled containers. Recommended storage temperature is 5°C - 25°C | |||||
Shelf Life: | None | |||||
Pot Life: | 20 – 30 minutes on substrate, abt. 15 minutes in the mixing container. | |||||
Flash Point: | >100˚C | |||||
Coverage (for a flat substrate): | Practical coverage depends on the porosity and evenness of the substrate and on the application method. |
Drying Times At 23°C | |
---|---|
Dust Dry: | After 6 hours |
Light trucking: | After 24 hours |
Fully Cured: | After 7 days |
Surface Preparation
New Concrete
- Remove laitance by power grinding vacuum grit blasting or hydrochloric acid etching.
- Choose the method best suited for the premises.
- After grinding remove dust carefully with a vacuum cleaner.
- Hydrochloric acid etching is carried out with diluted hydrochloric acid (1 part concentrated hydrochloric acid, 4 parts water).
- Rinse with plenty of water.
- Dry the surface.
Old Concrete
- Remove all grease, oil, chemicals and other impurities by Maalipesu detergent.
- Remove old peeling paint layer by grinding.
- Choose the method best suited for the premises.
- Clean out pot-holes removing all loose friable material.
- Open cracks with e.g. an abrasive tool.
- Remove loose material and dust.
If cementitious screed is used, check compatibility with the levelling screed manufacturer.
Application Conditions
- The relative humidity of the concrete should not exceed 97%.
- The temperature of the ambient air, surface or coating should not fall below +15ºC during application or drying.
- Relative humidity of air should not exceed 70%.
Mixing Components
Mixing Ratio | ||
---|---|---|
Base: | 4 parts by volume | Temafloor PU |
Hardener: | 1 part by volume | 008 4011 |
- First stir base and hardener separately.
- Mix the correct proportions of base and hardener thoroughly (approx. 2 minutes to get homogenous mixture) by using a low speed industrial hand drill with a paddle.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface, weaken the properties of the coating and risk the success of the application.
Thickness | ||
---|---|---|
Film thickness 1 mm coverage approx: | 1 m²/litre | |
Film thickness 2 mm coverage approx: | 0.5 m²/litre |
Application
Priming:
- Prime using about 30% thinned Temafloor 400 epoxy varnish.
- Pour the varnish onto the floor and apply as much as is needed to impregnate the concrete surface.
- If necessary, repeat priming to get a non-porous surface.
- A porous priming coat will result in holes and air bubbles in the finished coating.
- Subsequent treatment can be carried out after 2 hours using "wet-on-wet" technique.
- Asphalt floors should be primed by applying unthinned Temafloor PU with a suitable steel or rubber trowel.
- Scatter sand of grain size Ø 0,1–0,6 mm on the fresh primer coat to ensure the screed adhesion and prohibit gliding of the screed.
- Remove loose sand with vacuum cleaner before coating with Temafloor PU.
Patching:
- Patch pot-holes and cracks with a mixture of unthinned Temafloor 400 epoxy varnish and dry, clean sand.
- Mixing ratio e.g. 1 part by volume of varnish mixture and 1–2 parts by volume of sand of grain size 0.1–0.6 mm.
- Sand the patched areas before overcoating, if necessary.
- Note! Concrete surface should always be primed before patching.
Topcoating
- Overcoating should be done within 16–24 hrs after priming.
- If the primed surface is not overcoated within 24 hrs, it should be abraded.
- Pour the mixture onto the floor and apply it with a trowel and level with a roller.
- Control that the thickness of layer is correct by observing coating consumption and by measuring the film thickness.
- Recommended layer thickness is 1.0–2.0 mm.
- Use spiked roller to finish the surface approx. 10–20 min after application. Spiked roller helps removing air bubbles from the coating.
Thinner/Cleaning
Thinner:
- Do not thin Temafloor PU polyurethane coating.
VOC
- VOC 2004/42/EC (cat A/j) 500 g/l (2010)
- Temafloor PU: max. VOC < 500 g/l
Health And Safety
Reaction to fire: BFL-s1 according to standard EN 13501-1
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial and professional use only.
Data sheet
- Manufacturer
- Tikkurila
- For Use By
- Professional Use
- For Use On
- Concrete
- Sheen
- Gloss
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 15L
- Base Type
- Polyurethane
- Mixing Ratio
- Base: 4 parts by volume - Hardener: 1 part by volume
- Coverage
- Depends on the porosity and evenness of the substrate and on the application method.
- Recommended Thinner/Cleaner
- Thinner 1061
- Density
- 1.4 g/cm³ - Hardener: 1,23 g/cm³
- Solids by Volume
- approx. 100%
- VOC
- 500 g/l
- Finish
- Gloss
- Size
- 15L
- UN Number
- Not regulated
- Touch Dry (at 23°C)
- After 6 hours
- Dry to Handle (at 23°C)
- After 24 hours
- Fully Cured (at 23°C)
- 7 days
- Pot Life
- 20–30 minutes on substrate, abt. 15 minutes in the mixing container.
- Suitable For Use On
- Concrete
- Suitable For Use On
- Concrete Floors
- Suitable For Use On
- Asphalt
- Finish
- Gloss
- Components
- 2K
- Product Usage Type
- Self Smoothing Screed
- Product Range
- Temafloor
- Colour Family
- Grey
- Colour Family
- Red
- Colour Family
- Black
- Average Application Thickness
- 1-2mm
- Product Type
- Polyurethane
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temafloor PU is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Temafloor 220W Primer
2 component solvent-free varnish used for priming of new and old concrete floors, especially where solventless and odourless products are needed. For priming of new and old concrete floors prior to laying Temafloor coatings and screeds. Good resistance against oil and grease. Suitable for priming of damp concrete (relative humidity of the...
Tikkurila Temafloor 25 Clear
1-component moisture curing polyurethane primer and topcoat with excellent resistance to abrasion. Easy to apply due to one component formulation. Dust binding and prevents impurities from being absorbed into the surface. For topcoating of mosaic floors. Excellent resistance to abrasion. For varnishing of concrete, asbestos cement and...
Tikkurila Temafloor 400
2-component solvent-free epoxy varnish. An excellent product for dust binding and priming of new and old concrete floors, especially where solventless and odourless products are needed. The lacquer can be used for patching when filled with sand. Used as a binder for Temafloor 4000 troweling screed and epoxy concrete. Used also as a topcoat...