Tikkurila Temazinc 99, a 2-component, polyamide cured zinc-rich epoxy paint providing superior cathodic protection for steel, used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions.
- Prequalified in the NORSOK system 1; an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
- Zinc content exceeds standard ISO 12944-5 requirements for zinc-rich primers
- Can be used without a topcoat on surfaces exposed to weathering
- Recommended for bridges, cranes and steel frameworks as well as steelwork and equipment in the forest and chemical industries, such as tubular bridges, conveyors etc
- For industrial and professional use only
Tikkurila Temazinc 99 is a two-component, polyamide cured zinc-rich epoxy paint that provides superior cathodic protection for steel, used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions.
Temazinc 99 is prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges.
Recommended for bridges, cranes and steel frameworks as well as steelwork and equipment in the forest and chemical industries, such as tubular bridges, conveyors etc.
For industrial and professional use only.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Technical Data
- Mixing Ratio
- Recommended Film Thicknesses & Theoretical Coverage
- Drying Times
- Surface Preparation
- Recommended Topcoats
- Application Conditions
- Application
- Mixing Components
- Thinner
- Cleaner
- Health And Safety
Features & Benefits
- Two-component
- Polyamide cured zinc-rich epoxy paint
- Prequalified in the NORSOK system 1 and therefore an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges
- The zinc content of Temazinc 99 exceeds the requirements of the standard ISO 12944-5 for zinc-rich primers
- Provides superior cathodic protection for steel
- Used as a primer in epoxy, polyurethane, acrylic and chlorinated rubber systems for steel surfaces exposed to severe climatic conditions
- Can be used without a topcoat on surfaces exposed to weathering
- Recommended for bridges, cranes and steel frameworks as well as steelwork and equipment in the forest and chemical industries, such as tubular bridges, conveyors etc
- For industrial and professional use only
Technical Data
Volume solids
- 55±2% (ISO 3233)
Specific gravity
- 2.6 kg / l (mixed)
VOC
- The Volatile Organic Compounds amount is 430 g/litre of paint.
- VOC content of the paint mixture (thinned 10% by volume) is 473 g/l.
Pot Life (23℃):
- 30 hours
Mixing Ratio
Base (Temazinc 99):
- 3 parts by volume
Hardener (008 7440):
- 1 part by volume
Recommended Film Thicknesses & Theoretical Coverage
Recommended film thicknesses | Theoretical coverage | |
---|---|---|
Wet | Dry | |
70µm | 40µm | 13.8 m²/l |
145µm | 80µm | 6.9 m²/l |
Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated.
Drying Times
DFT 40µm | 5℃ | 10℃ | 23℃ | 35℃ |
---|---|---|---|---|
Dust dry, after | 50 minutes | 20 minutes | 10 minutes | 5 minutes |
Touch dry, after | 2 hours | 1 hours | 30 minutes | 15 minutes |
Recoatable, min after | 5 hour | 3 hour | 1 hour | 30 minutes |
Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation.
Surface Preparation
- Oil, grease, salts and dirt are removed by appropriate means. (ISO 12944-4)
Steel surfaces:
- Blast clean to grade Sa2½. (ISO 8501-1)
- In order to get the best performance the surface profile should be medium grit. (ISO 8503-2)
Recommended Topcoats
- Temacoat GPL-S Primer
- Temacoat GF Primer
- Temacoat GPL-S MIO
- Temacoat GS 50
- Temacoat RM 40
- Temachlor 40
- Temacryl AR 50
- Temanyl MS Primer
- Temacoat Primer
- Temacoat SPA Primer
- Temacoat SPA 50
- Temabond ST 200
- Temabond ST 300
- Temasolid SC 60
- Fontecoat EP 50 Beige
Application Conditions
- All surfaces must be clean, dry and free from contamination.
- The temperature of the ambient air, surface and paint should not fall below 5ºC during application and drying.
- Relative humidity of the air should not exceed 80% during application and drying.
- The surface temperature of steel should remain at least 3°C above the dew point.
- Good ventilation and sufficient air movement is required in confined areas during application and drying.
Note! There is a natural tendency of this coating to chalk, discolour or yellow unevenly. It is recommended to use polyurethane topcoat when there are high aesthetical requirements on colour appearance.
Mixing Components
- First stir base and hardener separately.
- The correct proportions of base and hardener must be mixed thoroughly before use.
- Use power mixer for mixing.
- Insufficient mixing or incorrect mixing ratio will result in uneven drying of the surface and weaken the properties of the coating.
Application
- Agitate during application.
For airless spraying:
- The product is thinned approximately 0–10%.
- Recommended nozzle tip is 0.015"–0.021" and pressure 120–180 bar.
- Spray angle shall be chosen according to the shape of the object.
- Sharp edges, corners, weld seams and other areas difficult to cover properly by spray application should be coated by brush before the spray application.
For brush application:
- Product should be thinned according to the circumstances.
Thinners
Cleaners
Health And Safety
Containers are provided with safety labels, which should be observed. Further information about hazardous influences and protection are detailed in individual health and safety data sheets.
For industrial use only.
Data sheet
- Manufacturer
- Tikkurila
- Water / Solvent Based
- Solvent
- For Use On
- Steel
- Application Method
- Brush, spray
- Sheen
- Matt
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Pack Size
- 8L
- Base Type
- Zinc-rich epoxy
- Solvent
- Mixture - see safety data sheet
- Mixing Ratio
- 3:1
- Key Features
- Prequalified in the NORSOK system 1; an excellent choice for the most demanding application areas such as offshore environments, refineries, power plants and bridges.
- Coverage
- 6.9 m²/l to 13.8 m²/l
- Recommended Thinner/Cleaner
- 1031
- Unit Contents
- Base & hardener
- Compatible Topcoats
- Temacoat GPL-S Primer, Temacoat GF Primer, Temacoat GPL-S MIO & more - see description/data sheet
- Min. Application Temperature
- The temperature of the ambient air, surface and paint should not fall below 5ºC during application and drying.
- Solids by Volume
- 55±2% (ISO 3233)
- VOC
- The Volatile Organic Compounds amount is 430 g/litre of paint; VOC content of the paint mixture (thinned 10% by volume) is 473 g/l.
- Recommended Dry Film Thickness
- 40µm to 80µm
- Recommended Wet Film Thickness
- 70µm to 145µm
- UN Number
- UN1263
- Dry to Recoat (at 23°C)
- 1 hour
- Pot Life
- 30 hours (at 23℃)
- Specific Gravity
- 2.6 kg / l (mixed)
- Base Type
- Solvent-Based
- Base Type
- Epoxy
- Suitable For Use On
- Steel
- Finish
- Matt 6-10%
- Application Method
- Brush
- Application Method
- Spray
- Usages
- Cathodic Protection
- Usages
- Atmospheric
- Usages
- Zinc Rich /Cold Galvanising
- Product Usage Type
- Primer
- Product Range
- Temazinc
- Colour Family
- Grey
- Dry to Recoat (@ 20-25°C)
- 60 mins
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Tikkurila Temazinc 99 is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Tikkurila Fontecoat EP 50
Tikkurila Fontecoat EP 50, a two-component water-borne epoxy topcoat and a single-coat paint recommended for framework, service platforms, conveyors and other steelwork, machinery and equipment. The product has MED (Marine Equipment Directive) certificate no VTT-C-12360-15-18 and is thus accepted for painting surfaces inside ships. Huge...
Tikkurila Temabond ST 200
2 component high-solids, aluminium pigmented modified epoxy maintenance paint for demanding surfaces such as steel structures, railway vehicles, and infastructure in energy and telecommunications. Surface-tolerant high-solids epoxy paint. Very good adhesion even to hand-prepared steel. Lower VOC emissions than conventional epoxy paints....
Tikkurila Temabond ST 300
Tikkurila Temabond ST 300 is a two-component high-solids, modified tintable epoxy maintenance paint for demanding surfaces, and is recommended for repairing of damages caused by transport or installation. Surface-tolerant with a wide colour range For steel and concrete surfaces Very good adhesion, even to hand-prepared steel Lower VOC...
Tikkurila Temachlor 40
Tikkurila Temachlor 40 is a one-component high-build chlorinated rubber-based paint that can be applied at sub-zero temperatures, as a finishing coat for chlorinated rubber systems Huge colour selection from RAL, BS & NCS Ideal steel surfaces and structures Good film-building properties Suitable for surfaces exposed to marine or...
Tikkurila Temacoat GF Primer
Tikkurila Temacoat GF Primer is a two component, polyamide cured epoxy primer containing zinc phosphate that is used as a primer for steel, zinc and aluminium surfaces. For industrial and professional use only For use in epoxy and polyurethane systems For use where high requirements for appearance are set Recommended for agricultural...
Tikkurila Temacoat GPL-S MIO
Tikkurila Temacoat GPL-S MIO is a two-component, polyamide cured epoxy paint pigmented with micaceous iron oxide, with superior adhesion to steel surfaces forming a very strong and durable film that can be used as a primer or an intermediate coat in aggressive environments Fast cure and low-temperature cure hardeners available - click to...
Tikkurila Temacoat GS 50
Tikkurila Temacoat GS 50, a two-component, polyamide-cured high build epoxy finishing and intermediate coat for protection of steel framework, conveyors, tubular bridges and other steel structures from abrasion and mechanical and/or chemical stress. Fast cure hardener available on request Can also be used as a sealer or a single-coat paint...
Tikkurila Temacoat Primer
A two-component resin modified epoxy paint containing anti-corrosive pigments that can be applied at sub-zero temperatures as a primer or an intermediate coat on surfaces exposed to climatic, mechanical and chemical stress. Recommended for building frameworks, tubular bridges, conveyors and other steelwork and equipment Adheres well to...
Tikkurila Temacoat RM 40
2-component, resin modified epoxy primer/topcoat with 4,000+ colours that can be used as a single-coat system. Good adhesion to steel, zinc and aluminium surfaces exposed to severe abrasion or chemical stress. Suitable for concrete surfaces and has a CE marking. Can be used on steel structures in wet environments, e.g. inside pontoons,...
Tikkurila Temacoat SPA 50
Tikkurila Temacoat SPA 50 is a two-component resin modified epoxy paint that can be applied to steel, zinc and aluminium as an excellent primer, intermediate or finish coat on surfaces exposed to stress and is also suitable as a single-coat system. Rapidly recoatable and ready to handle paint Forms durable film with good mechanical,...
Tikkurila Temacoat SPA Primer
Tikkurila Temacoat SPA Primer, a two-component resin modified epoxy primer with anti-corrosive pigments with excellent adhesion to steel, zinc and aluminium surfaces, that can be applied in thick layers, thus enabling faster production. Has high solids content Used as a primer or an intermediate coat in paint systems exposed to abrasion...
Tikkurila Temacryl AR 50
Tikkurila Temacryl AR 50, a physically drying, one-component semi-gloss acrylic based topcoat that can be applied at sub-zero temperatures on surfaces exposed to marine or industrial climates and mild chemical stress. Huge colour range available with RAL, BS & NCS shades Easy to handle in the painting process High film-building...
Tikkurila Temanyl MS Primer
Tikkurila Temanyl MS Primer is a one-component modified vinyl primer. Ideal for use on internal and external steel structures. Easy to handle in the painting process. Due to its high film-building properties, the paint can be applied in thick layers, thus shortening the application process. Can be applied at sub-zero temperatures, thus...
Tikkurila Thinner 1031
Tikkurila Thinner 1031 is a thinner for epoxy paints, silicone paints, polyvinylbutyral paints, 2-component zinc rich paints and epoxy shop primers.
Tikkurila Temasolid SC 60
Tikkurila Temasolid SC 60 is a two-component semi-gloss polyaspartic paint, containing anti-corrosive pigments. It has a high solids content and low VOC which reduces application time. Huge colour range available. Reduces application time and maximises production throughout at normal room temperature conditions without need for forced...
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...