Axalta Stokes Etch Primer Chromate-Free is a single pack pvb etch primer, chromate-free, for steel and non-ferrous metals.
- Formulated to be free from zinc chromate to EU Legislation 2007
- Use as an adhesion promoter for degreased galvanising, aluminium, copper, brass, nickel, and cadmium
- Also suitable for aluminium cladding, galvanised structures, and railings
- Can be overcoated with a wide range of both single pack and two pack products
- 14 ± 2% volume solids
Axalta Stokes Etch Primer Chromate-Free is a heat resistant, silicone resin based, aluminium finish used as an adhesion promoter for degreased galvanising, aluminium, copper, brass, nickel, and cadmium. Also suitable for aluminium cladding, galvanised structures, and railings, Axalta Stokes Etch Primer Chromate-Free is formulated to be free from zinc chromate to EU Legislation 2007. Can be overcoated with a wide range of both single pack and two pack products.
Click To Jump To Section:
- Features and Benefits
- Product Specification
- Drying Times
- Surface Preparation
- Application Methods
- Application Conditions
- Health and Safety
Features and Benefits
- Formulated to be free from zinc chromate to EU Legislation 2007
- Use as an adhesion promoter for degreased galvanising, aluminium, copper, brass, nickel, and cadmium
- Also suitable for aluminium cladding, galvanised structures, and railings
- Can be overcoated with a wide range of both single pack and two pack products
Product Specification
Technical Data | |
---|---|
Stokes Etch Primer Chromate-Free | |
Volume Solids: | 14 ± 2% (varies with colour) |
Theoretical Coverage Rate: |
11.6 m²/litre Practical coverage depends on the application method, painting conditions and the shape and roughness of the surface to be coated |
Dry Film Thickness: | 12 µm |
Wet Film Thickness: | 86 µm |
VOC Values: | 700 + 20 g/litre (varies with colour) |
SG: | 0.93 kg/lt (varies with colour) |
Flash Point: | Below 23ºC – low flash material |
Shelf Life: | Minimum 6 months if stored as above in unopened containers |
Drying Times
Curing Schedule | ||||
---|---|---|---|---|
Applied to 15 microns DFT | +10ºC | +23ºC | +35ºC | |
Dust Free | 20 min | 10 min | 5 min | |
Hard Dry | 60 min | 30 min | 15 min | |
Overcoating | Minimum | 60 min | 30 min | 15 min |
Maximum | See Product Notes |
- Drying and recoating times are related to the film thickness, temperature, the relative humidity of the air and ventilation
Surface Preparation
Carbon Steel (Non-Blasted)
- Thoroughly degrease and prepare to St2 (ISO 8501- 1:2007) taking care to avoid ‘polishing’ the surface
Non-Ferrous Metals
- Thoroughly degrease using a propriety biodegradable degreaser to remove all verdigris, salts and other contaminants
- Wash with clean fresh water and allow to dry
- Very smooth or glossy areas should be lightly abraded to provide a ‘key’
General
- All surfaces to be coated should be dry and cleaned as necessary to remove all oil, grease, salts, weld flux or other contamination. Where necessary, remove weld spatter and grind smooth all sharp edges and weld seams
Application Methods
Product Information | |
---|---|
Mixing: | Must be mixed thoroughly by using a mechanical agitator before use. Agitate periodically to ensure paint remains homogeneous. |
Thinning: | Thinner TH001 |
Equipment Cleaner: Thinner TH001 | |
Conventional Spray: | Use 40-60psi pressure with 1.4-1.6mm nozzle, thin as required |
Airless Spray: |
Output fluid pressure at tip 1500-2500 psi Tip size: 9-13 thou (0.23-0.33mm) Thin as required |
Brush and Roller: | Brush or roller application should be used for edges and small areas only, thin as required |
- This product would normally be spray applied, with conventional spray preferred, as airless spray may result in over-application
- DO NOT OVER APPLY or splitting of primer by topcoats may result
- Do not exceed the recommended dry film thickness
- Should not be applied or cured at temperatures below 4ºC. Temperature should preferably remain at a minimum of 10ºC
- Do not use on surfaces operating above of 60ºC
- Must be protected from weathering prior to being recoated
- Caution - contains phosphoric acid
- Low flash material - ventilate to keep solvent vapour levels below minimum explosive limit and observe low flash regulations
Application Conditions
- Only apply in conditions of good ventilation which must be maintained during drying and curing
- Do not apply when rain, mist, sleet, or snow are imminent
- During application and drying time of the paint coating, the surface should be dry, the Relative Humidity should not exceed 85% and the steel temperature should remain at least 3°C above the dew point
- Only apply this product when the above conditions can be maintained throughout the critical application and drying/curing process
- Paint temperature should ideally be at a minimum of 15ºC
Health and Safety
- Containers are provided with safety labels which should be observed
- Further information about hazardous influences and protection are detailed in individual product safety data sheets in the attachments section above.
Data sheet
- Manufacturer
- Axalta Coating Systems
- For Use On
- Carbon Steel, Non-Ferrous Metal
- Application Method
- Brush, Roller, Spray
- Sheen
- Matt
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Single
- Pack Size
- 5L
- Coverage
- 11.6 m²/litre
- Recommended Thinner/Cleaner
- TH001 Thinner
- Max. Application Temperature
- 10ºC
- Min. Application Temperature
- 4ºC
- Solids by Volume
- 14 ± 2% (varies with colour)
- VOC
- 700 + 20 g/litre (varies with colour)
- Shelf Life (from date of manufacture)
- Minimum 6 months if stored as above in unopened containers
- Recommended Dry Film Thickness
- 12 µm
- Recommended Wet Film Thickness
- 86 µm
- UN Number
- UN1263, UN3469
- Hard Dry
- +10ºC: 60 min, +23ºC: 30 min, +35ºC: 15 min
- Base Type
- Solvent-Based
- Base Type
- Polyvinyl Butyral
- Suitable For Use On
- Aluminium
- Suitable For Use On
- Galvanised Steel
- Suitable For Use On
- Copper
- Suitable For Use On
- Brass
- Suitable For Use On
- Nickel
- Suitable For Use On
- Cadmium
- Application Method
- Roller
- Application Method
- Spray
- Application Method
- Brush
- Usages
- Adhesion Promoting
- Usages
- Atmospheric
- Product Usage Type
- Primer
- Product Range
- Stokes
- Fastest Delivery
- Next Working Day
- Colour Family
- Grey
- Dry to Recoat (@ 20-25°C)
- 30 mins
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Axalta Stokes Etch Primer Chromate-Free is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Axalta Thinner TH001
Axalta Thinner TH001, for use with the Axalta range of coatings, has a specially formulated blend of solvents designed to mix with its compatible paint/coating to create an optimal consistency for application whether it be for brush, roller or spray Can also be used for the cleaning of some surfaces prior to application of the coating...
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...