Jotun Jotamastic 90 Aluminium WG is a two component winter grade polyamine cured epoxy mastic coating. It is aluminium pigmented for improved barrier effect. Suitable for properly prepared carbon steel, galvanised steel, stainless steel, aluminium, concrete and a range of aged coating surfaces.
- Winter grade version of Jotamastic 90 Aluminium to aid application in lower temperatures (from -5 °C)
- Surface tolerant, abrasion resistant, high solids, high build product
- Specially designed for areas where optimum surface preparation is not possible or required
- Provides long lasting protection in environments with high corrosivity
- Can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments
- Approved for PSPC for Crude Oil Tanks according to IMO Res. MSC 288(87) NORSOK System 1, Rev.5
Jotun Jotamastic 90 Aluminium WG is a two component winter grade polyamine cured epoxy mastic coating. It is a surface tolerant, abrasion resistant, high solids, high build product. This product is the winter grade version of Jotamastic 90 Aluminium to aid application in lower temperatures (from -5 °C) and to provide faster drying and curing times.
This version of Jotun Jotamastic 90 WG is aluminium pigmented for improved barrier effect. Specially designed for areas where optimum surface preparation is not possible or required.
Jotun Jotamastic 90 Aluminium WG provides long lasting protection in environments with high corrosivity and can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments. Suitable for properly prepared carbon steel, galvanised steel, stainless steel, aluminium, concrete and a range of aged coating surfaces.
Primarily designed for maintenance and repair for general use. It can also be used in marine environments for outside hulls, exterior and interior areas.
Jotun Jotamastic 90 Aluminium WG is recommended as a protective coating for offshore environments, including splash zones, refineries, power plants, bridges, buildings, mining equipment and general structural steel.
Quick Links - Click To Jump To Section:
- Features & Benefits
- Approvals & Certificates
- Product Data
- Film Thickness
- Surface Preparation
- Application
- Drying & Curing Time
- Heat Resistance
- Product Compatibility
- Storage & Shelf Life
- Caution
- Health & Safety
Features & Benefits
- Winter grade version of Jotamastic 90 Aluminium to aid application in lower temperatures (from -5 °C) and to provide faster drying and curing times
- Aluminium pigmented for improved barrier effect
- Two component polyamine cured epoxy mastic coating
- Surface tolerant, abrasion resistant, high solids, high build product
- Specially designed for areas where optimum surface preparation is not possible or required
- Provides long lasting protection in environments with high corrosivity
- Can be used as primer, mid coat, finish coat or as single coat system in atmospheric and immersed environments
- Touch dry in 3.5 hours at 23 °C
- Approved for PSPC for Crude Oil Tanks according to IMO Res. MSC 288(87) NORSOK System 1, Rev.5
- Suitable for properly prepared carbon steel, galvanised steel, stainless steel, aluminium, concrete and a range of aged coating surfaces
- Primarily designed for maintenance and repair for general use
- It can also be used in marine environments for outside hulls, exterior and interior areas
- Recommended as a protective coating for offshore environments, including splash zones, refineries, power plants, bridges, buildings, mining equipment and general structural steel
Approvals & Certificates
- Approved for PSPC for Crude Oil Tanks according to IMO Res. MSC 288(87)
- NORSOK System 1, Rev.5
- Grain, Newcastle Occupational Health
- When used as part of an approved scheme, this material has the following certification:
- Low Flame Spread in accordance with EU Directive for Marine Equipment
- Approved in accordance with parts 5 and 2 of Annex 1 of IMO 2010 FTP Code, or Parts 5 and 2 of Annex 1 of IMO FTPC when in compliance with IMO 2010 FTP Code Ch. 8
Additional certificates and approvals may be available on request.
Product Data
Technical Data | |
---|---|
Solids by volume | 80 ± 2 % |
Gloss level (GU 60 °) | Semi Gloss (35-70) |
Flash point | 36 °C |
Density | 1.4 kg/l |
VOC-EU | 213 g/l |
The provided data is typical for factory produced products, subject to slight variation depending on colour.
All data is valid for mixed paint.
Small colour variations may occur when changing between the two curing agents. If exposed to weathering without topcoat, the Wintergrade (WG) version will yellow at a faster rate than the same colour in Standard grade.
Film Thickness
Recommended Film Thicknesses | Theoretical Spreading Rate | |
---|---|---|
Dry | Wet | |
100µm | 125µm | 8m²/l |
300µm | 375µm | 2.7m²/l |
Surface Preparation
To secure lasting adhesion to the subsequent product all surfaces shall be clean, dry and free from any contamination.
Surface Preparation | ||
---|---|---|
Substrate | Minimum | Recommended |
Carbon Steel | St 2 (ISO 8501-1) | Sa 2½ (ISO 8501-1) |
Stainless Steel | The surface shall be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratch pattern to the surface | Abrasive blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface profile |
Aluminium | The surface shall be hand or machine abraded with non-metallic abrasives or bonded fibre machine or hand abrasive pads to impart a scratch pattern to the surface | Abrasive blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface profile |
Galvanised Steel | Abrasive blast cleaning to achieve a surface profile using non-metallic abrasive media which is suitable to achieve a sharp and angular surface profile | Sweep blast-cleaning using non-metallic abrasive leaving a clean, rough and even pattern |
Shop Primed Steel | Clean, dry and undamaged shop primer (ISO 12944-4 5.4) | Sa 2 (ISO 8501-1) |
Coated Surfaces | Clean, dry and undamaged compatible coating | Clean, dry and undamaged compatible coating |
Concrete | Low pressure water washing to a rough, clean, dry and laitance free surface. | Minimum 4 weeks curing. Moisture content maximum 5 %. Prepare the surface by means of enclosed blast shot or diamond grinding and other appropriate means to abrade the surrounding concrete and to remove laitance |
Please refer to the Application Guide (AG) for full details.
Application
Application Methods:
- Spray: Use airless spray
- Brush: Use a suitable brush. Care must be taken to achieve the specified dry film thickness
- Roller: May be used for small areas. Not recommended for first primer coat. Care must be taken to achieve the specified dry film thickness
Please refer to the Application Guide (AG) for full details.
Product Mixing:
- Jotamastic 90 Alu Comp A - 3.5 part
- Jotamastic 90 Winter Grade Comp B - 1 part
Pot Life:
- 45 minutes @ 23°C
Thinner/Cleaning Solvent:
- Thinner: Jotun Thinner No. 17
Guiding Data for Airless Spray:
- Nozzle tip (inch/1000): 19-25
- Pressure at nozzle (minimum): 150 bar/2100 psi
Drying & Curing Time
Substrate Temperature | -5 °C | 0 °C | 5°C | 10°C | 23°C | 40°C |
---|---|---|---|---|---|---|
Surface (touch) dry | 24 h | 18 h | 12 h | 8 h | 3.5 h | - |
Walk-on-dry | 72 h | 30 h | 20 h | 12 h | 4 h | - |
Dry to over coat, minimum | 54 h | 20 h | 10 h | 6 h | 2 h | - |
Dried/cured for service | 21 d | 14 d | 10 d | 5 d | 3 d | - |
- For maximum overcoating intervals, refer to the Application Guide (AG) for this product
- Drying and curing times are determined under controlled temperatures and relative humidity below 85 %, and at average of the DFT range for the product
- Surface (touch) dry: The state of drying when slight pressure with a finger does not leave an imprint or reveal tackiness
- Walk-on-dry: Minimum time before the coating can tolerate normal foot traffic without permanent marks, imprints or other physical damage
- Dry to over coat, minimum: The recommended shortest time before the next coat can be applied
- Dried/cured for service: Minimum time before the coating can be permanently exposed to the intended environment/medium
Heat Resistance
Temperature | ||
---|---|---|
Continuous | Peak | |
Dry, atmospheric | 120 °C | - |
Peak temperature duration max. 1 hour.
The temperatures listed relate to retention of protective properties. Aesthetic properties may suffer at these temperatures.
Note that the coating will be resistant to various immersion temperatures depending on the specific chemical and whether immersion is constant or intermittent. Heat resistance is influenced by the total coating system. If used as part of a system, ensure all coatings in the system have similar heat resistance.
Product Compatibility
Depending on the actual exposure of the coating system, various primers and topcoats can be used in combination with this product. Some examples are shown below.
Previous Coat:
- Epoxy shop primer, inorganic zinc silicate shop primer, zinc epoxy, epoxy, epoxy mastic, inorganic zinc silicate
Subsequent coat:
- Polyurethane, polysiloxane, epoxy, acrylic, vinyl epoxy
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Storage & Shelf Life
Shelf life at 23 °C
- Jotamastic 90 Alu Comp A - 48 Months
- Jotamastic 90 Winter Grade Comp B - 24 Months
In some markets commercial shelf life can be dictated shorter by local legislation. The above is minimum shelf life, thereafter the paint quality is subject to re-inspection.
Caution
- This product is for professional use only
- The applicators and operators shall be trained, experienced and have the capability and equipment to mix/stir and apply the coatings correctly and according to Jotun's technical documentation
- Applicators and operators shall use appropriate personal protection equipment when using this product
- This guideline is given based on the current knowledge of the product
- Any suggested deviation to suit the site conditions shall be forwarded to the responsible Jotun representative for approval before commencing the work
Health & Safety
- Please observe the precautionary notices displayed on the container
- Use under well ventilated conditions
- Do not inhale spray mist
- Avoid skin contact
- Spillage on the skin should immediately be removed with suitable cleanser, soap and water
- Eyes should be well flushed with water and medical attention sought immediately
Please contact Rawlins Paints' Technical Support Team on 0113 2455450 (option 2) or send a message to [email protected] for more information.
Data sheet
- Manufacturer
- Jotun
- For Use By
- Professional Use
- Interior / Exterior Use
- Interior & Exterior
- For Use On
- Steel, Carbon Steel, Stainless Steel, Aluminium, Galvanized Steel, Shop Primed Steel, Concrete
- Application Method
- Airless Spray, Brush, Roller
- Sheen
- Semi-Gloss
- Colour
- Standard / Ready Mixed
- Single, Two or Three Pack
- Two-Pack
- Product Certifications
- Approved for PSPC for Crude Oil Tanks according to IMO Res. MSC 288(87) NORSOK System 1, Rev.5
- Pack Size
- 4.55L, 20L
- Minimum Applied Thickness
- 100μm DFT
- Maximum Applied Thickness
- 300μm DFT
- Mixing Ratio
- 3.5/1
- Touch Dry (at 20°C)
- 3.5 hours
- Coverage
- 2.7 - 8m²/l
- Recommended Thinner/Cleaner
- Jotun Thinner No. 17
- Max. Application Temperature
- 40°C
- Min. Application Temperature
- -5°C
- Density
- 1.4 kg/l
- Solids by Volume
- 80 ± 2 %
- Heat Resistance (up-to)
- 120°C
- Shelf Life (from date of manufacture)
- Jotamastic 90 Alu Comp A - 48 Months, Jotamastic 90 Winter Grade Comp B - 24 Months
- UN Number (Activator)
- UN1263
- UN Number (Base)
- UN1263
- Dry to Recoat (at 23°C)
- 2 hours
- Touch Dry (at 23°C)
- 3.5 hours
- Fully Cured (at 23°C)
- 3 days
- Base Type
- Solvent-Based
- Suitable For Use On
- Concrete
- Suitable For Use On
- Aluminium
- Suitable For Use On
- Stainless Steel
- Suitable For Use On
- Steel
- Suitable For Use On
- Galvanised Steel
- Suitable For Use On
- Shop Primed Steel
- Suitable For Use On
- Immersion
- Suitable For Use On
- Primed Surfaces
- Suitable For Use On
- Compatible Existing Coatings
- Finish
- Semi-Gloss
- Application Method
- Brush
- Application Method
- Roller
- Application Method
- Spray
- Usages
- High Solids
- Usages
- High Build
- Usages
- Abrasion Resistant
- Usages
- Low Temperature
- Usages
- Surface Tolerant
- Usages
- Atmospheric
- Usages
- Immersion
- Usages
- 1 Coat
- Usages
- High Corrosivity Environments
- Usages
- Direct to Metal
- Product Usage Type
- Primer & Topcoat
- Product Range
- Jotamastic
- Colour Family
- Aluminium
- Categorised As
- Metal Paints > Low Temperature Direct-to-Metal Paints
- Seasonal
- Cold Weather
- Product Type
- Epoxy Mastic
- Environment
- Immersion
- Environment
- Atmospheric
- Environment
- Low Temperature
- Environment
- High Corrosivity Environments
- Touch Dry/Dust Free (@ 20-25°C)
- 3.5 hours
- Product Attributes
- 1 coat
- Product Attributes
- High Build
- Product Attributes
- High Solids
- Product Attributes
- Surface Tolerant
- Resistance to
- Abrasion
Questions
Question about the product
Be the first to ask a question about this product!
IMPORTANT SHIPPING & DELIVERY INFORMATION
Jotun Jotamastic 90 Aluminium WG is only available with the shipping and delivery timescales listed below - please do not contact our Customer Support Team with enquiries about alternative or earlier shipping and delivery times.
Saturdays and Sundays, as well as Bank Holidays, are not classed as working days.
Orders placed after the cut-off for this product will not be processed for earliest dispatch until 9am the next working day.
All delivery costs below are excluding VAT
Jotun Jotamastic 90 WG
Jotun Jotamastic 90 WG is a winter grade version of Jotamastic 90 to aid application in lower temperatures and to provide faster drying and curing times. Two component polyamine cured epoxy mastic coating Also available as Jotun Jotamastic 90 Aluminium WG for improved barrier effect Surface tolerant Abrasion resistant High solids High...
Jotun Thinner No. 17
Jotun Thinner No. 17 is a paint thinner designed to improve the flow of a range of Jotun epoxy products. It can also be used as cleaner of pumps and tools after and before painting. Jotun Thinner No. 17 is specially suitable as a thinner for epoxies and similar type products except Tankguard series.
Jotun Jotamastic 90 Aluminium
Jotun Jotamastic 90 Aluminium is a two component polyamine cured epoxy mastic coating. It is aluminium pigmented for improved barrier effect. Suitable for properly prepared carbon steel, galvanised steel, stainless steel, aluminium, concrete and a range of aged coating surfaces. Aluminium version of Jotun Jotamastic 90 Surface tolerant,...
Surface Preparation Kits for Steel
These surface preparation kits for steel have been created to help provide customers with an easily accessible bundle of tools to aid in the preparation of steel surfaces in accordance with ISO 8501-1 (St2/3) and SSPC (SP 2/3). Please click here for important information about these kits. Kit Contents: SET 1 (Hand Tools) 1 x Rust-Oleum...