Features & Benefits

• Stable to steam cleaning and hot water exposure at a thickness of 9mm
• Very high chemical resistance
• Suitable for cold storage and freezer rooms
• Water-based and non-tainting
• Seamless
• High abrasion resistance
• Slip resistant
• Lightly textured matt finish
• Designed for use in a wide range of heavy to very heavy duty industrial environments where a lasting solution to floor maintenance is required
• Ideal for both wet and dry processing environments, such as the food, beverage and chemical industries, heavy engineering plants, oil refineries, electricity stations and battery rooms
• Contains a white aggregate which imparts a slip resistant profile to the finished floor. When first installed, the floor has a uniform coloured surface. However, with general use, the white aggregate will begin to show through giving a decorative, mottled appearance

Application Notes

• Nitoflor SL2000 U should be applied as a primer/ scratch coat at a coverage rate of up to a nominal 1 mm thickness
• A rotary drum mixer is required. Pre mixing of the coloured liquid base component in its packaging is essential to ensure any light settlement is reincorporated
• Apply to primed areas to the required thickness using a steel float. Ensure that anchorage grooves are fully wetted out with material
• The cured product should be protected from other trades using Kraft paper or similar breathable material. Polythene should not be used. Protect the installed floor from damp, condensation and water for at least 4 days
• Regular cleaning is essential to enhance and maintain the life expectancy, slip resistance and appearance of the floor. Cured product can be easily cleaned using industry standard cleaning chemicals and techniques
• When applied at 9mm thickness, Fosroc Nitoflor RT6000 US is steam cleanable using a moving lance

Limitations

• Do not proceed with application if atmospheric relative humidity is, or is anticipated to be, >90% or if the surface temperature is <3ºC above the dew point
• Application should not commence when the substrate temperature or the ambient temperature is, or is anticipated to be, <5ºC during the application or within the tack-free period. Application can take place below the ideal range of 15 - 25ºC, subject to a minimum of 10ºC, however the surface finish may be subject to e.g. trowel marks. The product should NOT be applied above 25ºC
• The design strength of concrete surfaces must be a minimum of 25 MPa compressive strength at 28 days
• The manufacture of Fosroc Nitoflor RT6000 US is a batch process and despite close manufacturing tolerances, colour variation may occur between batches
• Product is not colour fast and may yellow over time. The rate of change will depend on UV light and heat levels and cannot be predicted. This will be more pronounced with lighter colours and blue shades and does not compromise the product’s performance or chemical resistance characteristics